Influence of cyclic loading on the onset of failure in a Zr-based bulk metallic glass
Influence of cyclic loading on the onset of failure in a Zr-based bulk metallic glass
复制标题
循环载荷对锆基大块金属玻璃失效发生的影响
DOI：
10.1007/s10853-014-8276-2
复制
发表时间：
2014
影响因子：
4.5
通讯作者：
Louzguine-Luzgin D
中科院分区：
文献类型：
--
作者：
Louzguine-Luzgin D
对Zr62.5Cu22.5Fe5Al10大块非晶合金试样进行了单轴压缩实验。在单调加载和循环加载（反复加载到塑性开始，然后卸载）的测试的比较表明，玻璃的压缩塑性在循环加载下急剧降低。有人认为，这种效果来自应力逆转加速剪切集中的主导剪切带。与压缩-压缩疲劳结果的链接，以及金属玻璃的低周疲劳的后果被认为是。
Samples of Zr62.5Cu22.5Fe5Al10bulk metallic glass are subjected to uniaxial compression. Comparison of tests in monotonic loading and cyclic loading (repeated loading to the onset of plasticity, then unloading) shows that the compressive plasticity of the glass is drastically reduced under cyclic loading. It is argued that this effect arises from stress reversal accelerating the concentration of shear on a dominant shear band. The link with compression–compression fatigue results, and the consequences for low-cycle fatigue of metallic glasses are considered.
登录
查看更多内容
同时施加电流和低应力对块状金属玻璃进行成型
DOI：
--
发表时间：
2000
期刊：
影响因子：
--
作者：
A. Yavari;M. D. Oliveira;W. Botta
通讯作者：
W. Botta
大块非晶合金的低周疲劳
DOI：
--
发表时间：
2003
期刊：
影响因子：
--
作者：
Zhang Haifeng
通讯作者：
Zhang Haifeng
化学变化对铝基非晶合金带弯曲疲劳行为的影响
DOI：
--
发表时间：
2012
期刊：
Metallurgical and Materials Transactions. A
影响因子：
--
作者：
Chun;J. Lewandowski
通讯作者：
J. Lewandowski
样品几何形状对金属玻璃机械行为的影响
DOI：
--
发表时间：
2006
期刊：
影响因子：
--
作者：
F. X. liu;P. Liaw;Gongyao Y. Wang;C. Chiang;D. A. Smith;P. Rack;J. Chu;R. Buchanan
通讯作者：
R. Buchanan
DOI：
10.1098/rspa.1957.0170
发表时间：
1957-01-01
影响因子：
--
作者：
COTTRELL, AH;HULL, D
通讯作者：
HULL, D