Performance of TS-1-Coated Structured Packing Materials for Styrene Oxidation Reaction
Performance of TS-1-Coated Structured Packing Materials for Styrene Oxidation Reaction
复制标题
TS-1涂层规整填料在苯乙烯氧化反应中的性能
DOI：
10.1021/cs1001509
复制
发表时间：
2011-03
期刊：
影响因子：
12.9
通讯作者：
Yeung, King Lun
中科院分区：
文献类型：
--
作者：
Wang, Xiaobin;Zhang, Xiongfu;Wang, Yao;Liu, Haiou;Qiu, Jieshan;Wang, Jinqu;Han, Wei;Yeung, King Lun
钛硅分子筛-1（TS-1）涂覆在复杂几何形状的不锈钢填料环上，为改善传质过程提供了大的界面接触面积。采用有机连接剂组装沸石晶种，并通过水热再生在其表面沉积一层薄而均匀的TS-1催化剂。的TS-1层的化学，结构和催化性能进行了检查。与粉末相比，从TS-1涂覆的基底获得了一个数量级更高的苯乙烯转化率。催化剂对预处理敏感，在氮气中热处理比空气煅烧样品的转化率高30%。N2预处理后的催化剂活性损失小，再生性能好。
Titanium silicalite-1 (TS-1)-coated on stainless steel packing rings of complex geometries provided a large interfacial contact area for improving mass transport processes. Zeolite seeds were assembled using organic linker, and a thin uniform layer of TS-1 catalyst was deposited on the surface by hydrothermal regrowth. The chemical, structural, and catalytic properties of the TS-1 layer were examined. An order of magnitude higher styrene conversion rate was obtained from the TS-1-coated substrates compared with powder. The catalyst was sensitive to pretreatment, and heat treatment in nitrogen provided a 30% higher conversion rate than the air-calcined samples. The N2-pretreated catalyst displayed lower activity loss and better regenerability.
登录
查看更多内容
影响因子：
9.5
作者：
L. Au;K. Yeung
通讯作者：
L. Au;K. Yeung
影响因子：
5.5
作者：
M. A. Uguina;D. Serrano;G. Ovejero;R. Grieken;M. Camacho
通讯作者：
M. A. Uguina;D. Serrano;G. Ovejero;R. Grieken;M. Camacho
影响因子：
--
作者：
Wang, Qingfa;Wang, Li;Mi, Zhentao
通讯作者：
Mi, Zhentao
影响因子：
7.3
作者：
Y. Wan;J. Chau;K. Yeung;A. Gavriilidis
通讯作者：
Y. Wan;J. Chau;K. Yeung;A. Gavriilidis
影响因子：
7.3
作者：
S. Laha;R. Kumar
通讯作者：
S. Laha;R. Kumar