Superior cycle performance and high reversible capacity of SnO2/graphene composite as an anode material for lithium-ion batteries.
Superior cycle performance and high reversible capacity of SnO2/graphene composite as an anode material for lithium-ion batteries.
复制标题
SNO2/石墨烯复合材料作为锂离子电池的阳极材料的出色周期性能和高可逆能力。
DOI：
10.1038/srep09055
复制
发表时间：
2015-03-12
影响因子：
4.6
通讯作者：
Zhang J
中科院分区：
文献类型：
--
作者：
Liu L;An M;Yang P;Zhang J
利用微波反应体系，通过一步微波水热法制备了具有优异循环性能和高可逆容量的SnO2/石墨烯复合材料。通过X射线衍射、热重分析、傅里叶变换红外光谱、拉曼光谱、扫描电子显微镜、X射线光电子能谱、透射电子显微镜和高分辨率透射电子显微镜对SnO2/石墨烯复合材料进行了表征。沉积在石墨烯片上的 SnO2 颗粒尺寸小于 3.5nm。 SnO2/石墨烯复合材料在锂离子电池中表现出高容量和优异的电化学性能。电流密度为100 mA g−1时，首次充放电容量分别为2213和1402mA h g−1，库仑效率为63.35%。在100、300、500和700 mA g−1的电流密度下循环100次后，放电比容量分别保持在1359、1228、1090和1005 mA h g−1。即使在1000 mA g−1的高电流密度下，首次放电和充电容量也分别为1502和876 mA h g−1，并且在420次和1000次循环后放电比容量分别保持在1057和677 mA h g−1。 SnO2/石墨烯复合材料表现出稳定的循环性能和高的锂存储可逆容量。
SnO2/graphene composite with superior cycle performance and high reversible capacity was prepared by a one-step microwave-hydrothermal method using a microwave reaction system. The SnO2/graphene composite was characterized by X-ray diffraction, thermogravimetric analysis, Fourier-transform infrared spectroscopy, Raman spectroscopy, scanning electron microscope, X-ray photoelectron spectroscopy, transmission electron microscopy and high resolution transmission electron microscopy. The size of SnO2 grains deposited on graphene sheets is less than 3.5 nm. The SnO2/graphene composite exhibits high capacity and excellent electrochemical performance in lithium-ion batteries. The first discharge and charge capacities at a current density of 100 mA g−1 are 2213 and 1402 mA h g−1 with coulomb efficiencies of 63.35%. The discharge specific capacities remains 1359, 1228, 1090 and 1005 mA h g−1 after 100 cycles at current densities of 100, 300, 500 and 700 mA g−1, respectively. Even at a high current density of 1000 mA g−1, the first discharge and charge capacities are 1502 and 876 mA h g−1, and the discharge specific capacities remains 1057 and 677 mA h g−1 after 420 and 1000 cycles, respectively. The SnO2/graphene composite demonstrates a stable cycle performance and high reversible capacity for lithium storage.
登录
查看更多内容
简便超声合成具有高储锂能力的CoO量子点/石墨烯纳米片复合材料
影响因子：
17.1
作者：
Peng, Chengxin;Chen, Bingdi;Yang, Jinhu
通讯作者：
Yang, Jinhu
影响因子：
--
作者：
Park, Seung-Keun;Yu, Seung-Ho;Piao, Yuanzhe
通讯作者：
Piao, Yuanzhe
影响因子：
3.7
作者：
Ferrari, AC;Robertson, J
通讯作者：
Robertson, J
影响因子：
9.2
作者：
Guo, Jinxue;Jiang, Bin;Liu, Hongtian
通讯作者：
Liu, Hongtian
多孔石墨烯网络作为锂离子电池高性能负极材料
影响因子：
10.9
作者：
Fan, Zhuangjun;Yan, Jun;Wei, Fei
通讯作者：
Wei, Fei