Effects of strong network modifiers on Fe3+/Fe2+ in silicate melts: an experimental study
Effects of strong network modifiers on Fe3+/Fe2+ in silicate melts: an experimental study
复制标题
强网络改性剂对硅酸盐熔体中 Fe3 /Fe2 的影响：实验研究
DOI：
10.1007/s00410-017-1337-1
复制
发表时间：
2017
影响因子：
3.5
通讯作者：
Holtz F.
中科院分区：
文献类型：
--
作者：
Borisov A;Behrens H;Holtz F.
研究了CaO、Na2O和K2O对模拟多元硅酸盐熔体中铁/铁比的影响，温度范围为1450-1550 °C，空气总压力为1-atm。结果表明，这些网络修饰阳离子的加入导致了Fe3+/Fe2+比值的增加。网络修饰剂阳离子对Fe/Fe比值的影响按Ca <； Na <； K的顺序递增。提出了空气条件下预测SiO2–TiO2–Al2O3–FeO–Fe2O3–MgO–CaO–Na2O–K2O–P2O5melts中铁/亚铁比的经验公式。
The effect of CaO, Na2O, and K2O on ferric/ferrous ratio in model multicomponent silicate melts was investigated in the temperature range 1450–1550 °C at 1-atm total pressure in air. It is demonstrated that the addition of these network modifier cations results in an increase of Fe3+/Fe2+ratio. The influence of network modifier cations on the ferric/ferrous ratio increases in the order Ca < Na < K. Some old controversial conceptions concerning the effect of potassium on Fe3+/Fe2+ratio in simple model liquids are critically evaluated. An empirical equation is proposed to predict the ferric/ferrous ratio in SiO2–TiO2–Al2O3–FeO–Fe2O3–MgO–CaO–Na2O–K2O–P2O5melts at air conditions.
登录
查看更多内容
熔体成分对硅酸盐熔体中 Fe3 /Fe2 的影响：模拟多组分系统中铁/亚铁比率的步骤
影响因子：
3.5
作者：
Borisov A;Behrens H;Holtz F.
通讯作者：
Holtz F.
信件：一种在单气氛实验中控制碱金属氧化物活度的方法及其在测量硅酸盐熔体中NaO0.5相对活度系数中的应用
DOI：
--
发表时间：
2005
期刊：
影响因子：
--
作者：
H. O’Neill
通讯作者：
H. O’Neill
硅酸盐玻璃中的稀释 Fe3：Fe 氧化还原态和基体组成的结构效应。
影响因子：
3.5
作者：
V. Vercamer;Gérald Lelong;H. Hijiya;Y. Kondo;L. Galoisy;G. Calas
通讯作者：
G. Calas
互溶液体之间 K 和 Na 分配的实验研究
影响因子：
1.5
作者：
A. Borisov
通讯作者：
A. Borisov
玻璃成型熔体中的氧化还原过程
影响因子：
3.5
作者：
H. Schreiber
通讯作者：
H. Schreiber