Morphological instabilities and alignment of lamellar eutectics during directional solidification under a strong magnetic field
Morphological instabilities and alignment of lamellar eutectics during directional solidification under a strong magnetic field
复制标题
强磁场定向凝固过程中层状共晶的形态不稳定性和排列
DOI：
10.1016/j.actamat.2009.10.048
复制
发表时间：
2010-02
期刊：
影响因子：
9.4
通讯作者：
Esling, Claude
中科院分区：
文献类型：
--
作者：
Li, Xi;Ren, Zhongming;Fautrelle, Yves;Zhang, Yudong;Esling, Claude
The effects of a strong magnetic field on Al–Al2Cu and Pb–Sn lamellar eutectics during directional solidification have been investigated experimentally. The results show that the application of a strong magnetic field caused “tilting and oscillatory” morphological instabilities and deformation of the eutectic lamellae. Moreover, it was found that the Al–Al2Cu eutectic grain became aligned under a strong magnetic field and that with an increase in the magnetic field intensity this alignment was gradually enhanced. Further, the stresses caused by the magnetization force and the thermoelectric magnetic force during directional solidification under a strong magnetic field were analyzed and it was found that they are likely responsible for the “tilting and oscillatory” morphological instabilities and deformation. This is experimental evidence that the stresses imposed on a solid are capable of inducing the morphological instabilities of lamellar eutectics. The magnetic crystalline anisotropy of the Al2Cu phases and the growth relationship between the primary Al2Cu phase and the eutectic phases was investigated and it was found that the Al2Cu phase had a remarkable magnetic crystalline anisotropy which determined the growth of the Al–Al2Cu eutectic grain. Thus, alignment of the Al–Al2Cu eutectic grain under a strong magnetic field may be attributed to the magnetic crystalline anisotropy of the Al2Cu phase. Based on the growth behaviour of Al–Al2Cu and Pb–Sn lamellar eutectics under a strong magnetic field, an alignment model of lamellar eutectics during directional solidification under a strong magnetic field is proposed.
登录
查看更多内容
影响因子：
1.6
作者：
SodesawaToshiaki;NakajimaHirotaka;NozakiFumio
通讯作者：
SodesawaToshiaki;NakajimaHirotaka;NozakiFumio
影响因子：
3.5
作者：
D. P. Woodruff;J. Bikerman
通讯作者：
D. P. Woodruff;J. Bikerman
DOI：
10.1007/bf02647722
发表时间：
1988-12
期刊：
Metallurgical Transactions A
影响因子：
--
作者：
V. Seetharaman;R. Trivedi
通讯作者：
V. Seetharaman;R. Trivedi
影响因子：
1.8
作者：
W. Lawson;H. W. Kerr;M. Lewis
通讯作者：
W. Lawson;H. W. Kerr;M. Lewis
影响因子：
1.6
作者：
A. Katsuki;R. Tokunaga;Shin‐ichi Watanabe;Y. Tanimoto
通讯作者：
A. Katsuki;R. Tokunaga;Shin‐ichi Watanabe;Y. Tanimoto