The nano-eutectic in the microstructure of semisolid Mg–6Zn–1Y alloy
The nano-eutectic in the microstructure of semisolid Mg–6Zn–1Y alloy
复制标题
半固态Mg-6Zn-1Y合金显微组织中的纳米共晶
DOI：
10.1016/j.matlet.2015.12.070
复制
发表时间：
2016-03
影响因子：
3
通讯作者：
Yingbo Zhang
中科院分区：
文献类型：
--
作者：
D;an Yao;Yingbo Zhang
摘要研究了Mg-6 Zn-1 Y（at%）合金在540° C半固态下分别在20° C水和20° C空气中冷却后的显微组织。在水冷试样中发现了（α-Mg+ I相）纳米共晶。在TEM下研究了纳米共晶的细节。与慢冷凝固的面心二十面体I相相比，快冷凝固的二十面体I相是原始的。研究了纳米共晶中{01 1 <$1 $>} Mg <${τ 10} I−相和{10 1 <$0} Mg <$2 f I−相的取向关系。不同晶格结构的两相以半共格的方式匹配，表明界面处于低能状态。
Abstract The microstructures of Mg–6Zn–1Y (at%) alloys cooling in the 20° C water and 20° C air respectively from semisolid state at 540° C were investigated in this work. An (α-Mg+ I-phase) nano-eutectic was discovered in the water-cooled samples. The details of the nano-eutectic were investigated under TEM. Compared with the face-centered icosahedral I-phase solidified at slow cooling rate, the icosahedral type of I-phase solidified at fast cooling rate is primitive. The orientation relationship of the two phase in the nano-eutectic was also studied, namely {01 1 ̅ 1 ̅} Mg∥{τ 10} I− phase and {10 1 ̅ 0} Mg∥ 2 f I− phase. The two phases with different lattice structure matched as semi-coherent, which indicated that the interface was in a low energy state.
登录
查看更多内容
影响因子：
5.5
作者：
Singh A
通讯作者：
Singh A
影响因子：
2.7
作者：
J. Cahn;D. Shechtman;D. Gratias
通讯作者：
J. Cahn;D. Shechtman;D. Gratias
DOI：
10.1016/0956-716x(93)90584-f
发表时间：
1993-06-15
期刊：
SCRIPTA METALLURGICA ET MATERIALIA
影响因子：
--
作者：
LUO, ZP;ZHANG, SQ;ZHAO, DS
通讯作者：
ZHAO, DS
DOI：
10.1016/s1006-7191(08)60017-4
发表时间：
2008-02
期刊：
Acta Metallurgica Sinica (english Letters)
影响因子：
--
作者：
Z. M. Zhang;C. Xu;X. Guo
通讯作者：
Z. M. Zhang;C. Xu;X. Guo
DOI：
10.1080/01418610008212098
发表时间：
2000-05
期刊：
Philosophical Magazine A
影响因子：
--
作者：
A. Tsai;Y. Murakami;A. Niikura
通讯作者：
A. Tsai;Y. Murakami;A. Niikura