Stress-free two-way thermoelastic shape memory and field-enhanced strain in Ni52Mn24Ga24 single crystals
Stress-free two-way thermoelastic shape memory and field-enhanced strain in Ni52Mn24Ga24 single crystals
复制标题
Ni52Mn24Ga24 单晶的无应力双向热弹性形状记忆和场增强应变
DOI：
10.1063/1.1325388
复制
发表时间：
2000-11
期刊：
影响因子：
--
通讯作者：
W.S.Zhan
中科院分区：
文献类型：
--
作者：
W.H.Wang,G.H.Wu,J.L.Chen,C.H.Yu,S.X.Gao,;W.S.Zhan
在单晶Ni_（52）Mn_（24）Ga_（24）中发现了无应力双向热弹性形状记忆效应，其应变率为1.2%，温度滞后为6 K。在沿着测量方向施加1.2 T的偏置场时，变形可增强3倍以上，收缩率可达4.0%，或在垂直于测量方向施加1.2 T的偏置场时，变形可变为1.5%的膨胀。对于实现大的变形，磁场表现出更明显的贡献比外部应力对这种材料。这些特征可以归因于低水平的内应力和马氏体变体的择优取向。
Stress-free and two-way thermoelastic shape memory, with 1.2% strain and 6 K temperature hysteresis, has been found in single crystalline Ni52Mn24Ga24. The deformation can be enhanced more than three times, up to 4.0% shrinkage with a bias field 1.2 T applied along the measurement direction, or changed to 1.5% expansion by the 1.2 T applied perpendicular to the measurement direction. For achieving a large deformation, the magnetic field exhibits a more evident contribution than an external stress on this material. These characteristics can be attributed to the low level of internal stress and the preferential orientation of the martensitic variants.
登录
查看更多内容
影响因子：
3.2
作者：
S. J. Murray;M. Farinelli;C. Kantner;J. Huang;S. Allen;R. O'handley
通讯作者：
S. J. Murray;M. Farinelli;C. Kantner;J. Huang;S. Allen;R. O'handley
影响因子：
--
作者：
Tsunehiko Todoroki;H. Tamura
通讯作者：
Tsunehiko Todoroki;H. Tamura
DOI：
10.1201/9780849391088.ax2
发表时间：
2006-12
期刊：
--
影响因子：
--
作者：
V. Konchits
通讯作者：
V. Konchits
DOI：
10.1016/0956-716x(92)90168-e
发表时间：
1992-01
期刊：
Scripta Metallurgica Et Materialia
影响因子：
--
作者：
V. Kokorin;V. Martynov;V. Chernenko
通讯作者：
V. Kokorin;V. Martynov;V. Chernenko
影响因子：
2.1
作者：
Tickle, R;James, RD;Kokorin, VV
通讯作者：
Kokorin, VV