Evaluation of ultraviolet aging resistance of bitumen modified with isobutyltriethoxysilane surface organic grafted LDH
Evaluation of ultraviolet aging resistance of bitumen modified with isobutyltriethoxysilane surface organic grafted LDH
复制标题
异丁基三乙氧基硅烷表面有机接枝LDH改性沥青的抗紫外老化性能评价
DOI：
10.1016/j.conbuildmat.2020.118016
复制
发表时间：
2020-04
影响因子：
7.4
通讯作者：
Duan Wenfeng
中科院分区：
文献类型：
--
作者：
Zhang Canlin;Yu Jianying;Wang Ting;Xu Song;Hu Changbin;Duan Wenfeng
Isobutyltriethoxysilane surface organic grafted layered double hydroxide (OLDH) was prepared and utilized to improve the ultraviolet aging resistance of bitumen. The results of Fourier transform infrared (FTIR) and Static contact angle showed that isobutyltriethoxysilane has been grafted on the surface of LDH and the hydrophilic property of OLDH was observably weakened. The storage stability test indicated that OLDH had better compatibility and stability in bitumen compared with LDH, which was due to the decrease of hydroxyl and the introduction of organic group on the surface of LDH after isobutyltriethoxysilane organic grafting modification. Furthermore, OLDH modified bitumen showed more excellent high-temperature behavior than that of LDH modified bitumen. After ultraviolet aging, the performance of bitumen seriously deteriorated and the colloid stability notably decreased. Comparing with LDH, OLDH exhibited better in inhibiting the performance deterioration and gelefication of bitumen after ultraviolet aging, which implied that isobutyltriethoxysilane surface organic grafting modification was beneficial to strengthen the improvement of LDH on the ultraviolet aging resistance of bitumen.
登录
查看更多内容
高海拔地区含无机纳米二氧化钛高弹性沥青混合料性能评价
影响因子：
7.4
作者：
Zheng Dong;Qian Zhen dong;Li Pan;Wang Lin bing
通讯作者：
Wang Lin bing
胶粉化学成分和形态对沥青流变性能和自修复性能的影响
影响因子：
7.4
作者：
Liu, Gang;Liang, Yangshi;Gu, Xin
通讯作者：
Gu, Xin
不同紫外线吸收剂改性沥青老化的 FTIR 和流变学分析
影响因子：
7.4
作者：
Feng, Zhen-gang;Wang, Shu-juan;Li, Xin-jun
通讯作者：
Li, Xin-jun
影响因子：
7.4
作者：
Xiong Xu;Jianying Yu;L. Xue;Bianyang He;Wei-na Du;Huang Zhang;Ying Li
通讯作者：
Xiong Xu;Jianying Yu;L. Xue;Bianyang He;Wei-na Du;Huang Zhang;Ying Li
影响因子：
7.4
作者：
Cao, Zhilong;Chen, Meizhu;Xue, Lihui
通讯作者：
Xue, Lihui