Suppression of Twinning and Phase Transformation in an Ultrafine Grained 2 GPa Strong Metastable Austenitic Steel: Experiment and Simulation
Suppression of Twinning and Phase Transformation in an Ultrafine Grained 2 GPa Strong Metastable Austenitic Steel: Experiment and Simulation
复制标题
DOI：
10.1016/j.actamat.2015.06.053
复制
发表时间：
2015-09
期刊：
影响因子：
9.4
通讯作者：
Yongfeng Shen;N. Jia;Yandong Wang;Xin Sun;L. Zuo;D. Raabe
中科院分区：
文献类型：
--
作者：
Yongfeng Shen;N. Jia;Yandong Wang;Xin Sun;L. Zuo;D. Raabe
An ultrafine-grained 304 austenitic 18 wt.% Cr–8 wt.% Ni stainless steel with a grain size of ∼270 nm was synthesized by accumulative rolling (67% total reduction) and annealing (550 °C, 150 s). Uniaxial tensile testing at room temperature reveals an extremely high yield strength of 1890 ± 50 MPa and a tensile strength of 2050 ± 30 MPa, while the elongation reaches 6 ± 1%. Experimental characterization on samples with different grain sizes between 270 nm and 35 μm indicates that both, deformation twinning and martensitic phase transformation are significantly retarded with increasing grain refinement. A crystal plasticity finite element model incorporating a constitutive law reflecting the grain size-controlled dislocation slip and deformation twinning captures the micromechanical behavior of the steels with different grain sizes. Comparison of simulation and experiment shows that the deformation of ultrafine-grained 304 steels is dominated by the slip of partial dislocations, whereas for coarse-grained steels dislocation slip, twinning and martensite formation jointly contribute to the shape change.