Effect of Pr3Al11 nanoparticles on crystallite growth kinetics of nanocrystalline Mg
Effect of Pr3Al11 nanoparticles on crystallite growth kinetics of nanocrystalline Mg
复制标题
Pr3Al11纳米颗粒对纳米晶镁微晶生长动力学的影响
DOI：
10.1016/j.jallcom.2019.07.047
复制
发表时间：
2019-10
影响因子：
6.2
通讯作者：
Zhang Q A
中科院分区：
文献类型：
--
作者：
Zhou C Q;Zhang Q A
In order to understand the effect of Pr3Al11nanoparticles on crystallite growth kinetics of nanocrystalline Mg, the crystallite growth characteristics in a Mg−Pr3Al11composite and a pure Mg sample were comparatively investigated in this work. The crystallite growth exponents of nanocrystalline Mg in the Mg−Pr3Al11composite and pure Mg were determined asn= 5 andn= 4, respectively. Meanwhile, the activation energy for crystallite growth in Mg−Pr3Al11composite was calculated to be 118.8 kJ/mol, which is higher than 97.1 kJ/mol in pure nanocrystalline Mg. Further studies reveal that the rise of crystallite growth exponent and increase of activation energy in the Mg−Pr3Al11composite are primarily attributed to the pinning effect of Pr3Al11nanoparticles at crystallite boundaries of Mg.
登录
查看更多内容
具有增强动力学的 Mg2Ni 的形成：使用 MgH2 代替 Mg 作为起始材料
影响因子：
3.3
作者：
Zhao, Bin;Fang, Fang;Sun, Dalin;Zhang, Qingan;Wei, Shiqiang;Cao, Fenglei;Sun, Huai;Ouyang, Liuzhang;Zhu, Min
通讯作者：
Zhu, Min
NaAlH4 的脱/再氢化特征仅局限于纳米孔中
影响因子：
9.4
作者：
Li, Y.;Zhou, G.;Sun, D.
通讯作者：
Sun, D.
DOI：
--
发表时间：
1948-06
期刊：
Metals technology
影响因子：
--
作者：
C. S. Smith
通讯作者：
C. S. Smith
影响因子：
6.2
作者：
A. Poletaev;R. Denys;J. K. Solberg;B. Tarasov;V. Yartys
通讯作者：
A. Poletaev;R. Denys;J. K. Solberg;B. Tarasov;V. Yartys
DOI：
--
发表时间：
1948
期刊：
--
影响因子：
--
作者：
Christian Smith
通讯作者：
Christian Smith