Precipitate nanostructuring that enhances lattice compatibility in a Ti-Fe-Al alloy
Precipitate nanostructuring that enhances lattice compatibility in a Ti-Fe-Al alloy
复制标题
沉淀纳米结构，增强 Ti-Fe-Al 合金中的晶格相容性
DOI：
10.1016/j.scriptamat.2023.115476
复制
发表时间：
2023
影响因子：
6
通讯作者：
Mellor R
中科院分区：
文献类型：
--
作者：
Mellor R
在TiFeAl合金中发现了一种新的分级显微组织。TEM分析表明，透镜状的功能，由纳米级的有序的金属间化合物B2相包围的正交相的通道域。这种纳米结构减少了基体和沉淀物在透镜平面中的错配，从而提供了比完全由B2相组成的沉淀物更好的应变相容性。该合金表现出590 HV的优异维氏硬度。
A novel hierarchical microstructure has been identified in a TiFeAl alloy. TEM analysis revealed lens-like features that were comprised of nanoscale domains of an ordered intermetallic B2 phase enveloped by channels of an orthorhombic phase. This nanostructure reduced the misfit between the matrix and precipitates in the plane of the lenses, thereby providing better strain compatibility than precipitates consisting entirely of the B2 phase. The alloy demonstrated an exceptional Vickers hardness of 590 HV.
登录
查看更多内容
常规文章超晶格金属间析出物增强的新型β钛合金体系
影响因子：
6
作者：
A. J. Knowles;T. Jun;A. Bhowmik;N. Jones;T. B. Britton;F. Giuliani;H. Stone;D. Dye
通讯作者：
D. Dye
含有有序 β TiFe、α 和 omega 的二元 β 钛高温合金
影响因子：
6
作者：
Jones R
通讯作者：
Jones R
影响因子：
--
作者：
J. H. Potgieter;N. Maledi;M. Sephton;L. Cornish
通讯作者：
J. H. Potgieter;N. Maledi;M. Sephton;L. Cornish
影响因子：
56.9
作者：
Sato, J;Omori, T;Ishida, K
通讯作者：
Ishida, K