Preparation and characterization of silica-coated Fe3O4 nanoparticles used as precursor of ferrofluids
Preparation and characterization of silica-coated Fe3O4 nanoparticles used as precursor of ferrofluids
复制标题
铁磁流体前驱体二氧化硅包覆 Fe3O4 纳米颗粒的制备及表征
DOI：
10.1016/j.apsusc.2008.09.071
复制
发表时间：
2009-01-01
影响因子：
6.7
通讯作者：
Wei, Dong-Guang
中科院分区：
文献类型：
--
作者：
Hong, Ruo-Yu;Li, Jian-Hua;Wei, Dong-Guang
Fe3O4 magnetic nanoparticles (MNPs) were synthesized by the co-precipitation of Fe3+ and Fe2+ with ammonium hydroxide. The sodium citrate-modified Fe3O4 MNPs were prepared under Ar protection and were characterized by Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), X-ray powder diffraction (XRD) and vibrating sample magnetometer (VSM). To improve the oxidation resistance of Fe3O4 MNPs, a silica layer was coated onto the modified and unmodified MNPs by the hydrolysis of tetraethoxysilane (TEOS) at 50 degrees C and pH 9. Afterwards, the silica-coated Fe3O4 core/shell MNPs were modified by oleic acid (OA) and were tested by IR and VSM. IR results revealed that the OA was successfully grafted onto the silica shell. The Fe3O4/SiO2 core/shell MNPs modified by OA were used to prepare water-based ferrofluids (FFs) using PEG as the second layer of surfactants. The properties of FFs were characterized using a UV-vis spectrophotometer, a Gouy magnetic balance, a laser particle size analyzer and a Brookfield LVDV-III+ rheometer. (C) 2008 Elsevier B. V. All rights reserved.