Stress Corrosion Crack Growth Behavior of Type 310S Stainless Steel in Supercritical Water
Stress Corrosion Crack Growth Behavior of Type 310S Stainless Steel in Supercritical Water
复制标题
310S不锈钢在超临界水中的应力腐蚀裂纹扩展行为
DOI：
10.5006/2775
复制
发表时间：
2018-03
期刊：
影响因子：
1.6
通讯作者：
Andresen Peter L
中科院分区：
文献类型：
--
作者：
Chen Kai;Wang Jiamei;Du Donghai;Guo Xianglong;Zhang Lefu;Andresen Peter L
研究了310 S不锈钢在400°C ~ 550°C超临界水中的应力腐蚀行为。裂纹扩展速率（CGR）作为温度和腐蚀电位的函数。结果表明，310 S型不锈钢
Stress corrosion crack (SCC) behavior of Type 310S stainless steel (SS) in supercritical water was evaluated at 400°C to 550°C. Crack growth rates (CGR) were obtained as a function of temperature and corrosion potential. Results show that Type 310S SS exh