Variation of crystal orientation during epitaxial growth of dendrites by laser deposition
Variation of crystal orientation during epitaxial growth of dendrites by laser deposition
复制标题
激光沉积枝晶外延生长过程中晶体取向的变化
DOI：
10.1016/j.jmst.2017.05.002
复制
发表时间：
2017-05
期刊：
影响因子：
--
通讯作者：
Hu Zhuang-Qi
中科院分区：
文献类型：
--
作者：
Wang Guo-Wei;Liang Jing-Jing;zhou Yi-Zhou;Jin Tao;Sun Xiao-Feng;Hu Zhuang-Qi
采用外延激光金属成形（E-LMF）技术在单晶衬底上制备了镍基高温合金。研究了两种沉积层的微观组织发育。首次发现了当枝晶在沉积过程中发生偏转时，枝晶的取向变化超过20°。此外，在晶粒中不同取向枝晶之间发现了新的晶界，检测到的晶界角为23°。结果表明，激光池内的流动场是造成这一现象的主要原因。
A nickel-based superalloy was deposited onto a single crystal substrate based on epitaxial laser metal forming (E-LMF). The microstructure development in two depositions has been researched. For the first time, the crystal orientation of dendrites varying beyond 20° was found when the dendrites deflected in deposition. In addition, a new grain boundary was found between different orientation dendrites in a grain, and the detected grain boundary angle was 23°. The result shows that flowing field in laser pool is responsible for this phenomenon.
登录
查看更多内容
影响因子：
1.8
作者：
Robert Tönhardt;G. Amberg
通讯作者：
Robert Tönhardt;G. Amberg
基体取向对激光表面重熔单晶高温合金中等轴杂散晶粒形成的影响：实验研究
影响因子：
9.4
作者：
Wang, L.;Wang, N.
通讯作者：
Wang, N.
DOI：
10.1016/0001-6160(84)90030-0
发表时间：
1984-06
期刊：
Acta Metallurgica
影响因子：
--
作者：
K. Murakami;Hiroyuki Aihara;T. Okamoto
通讯作者：
K. Murakami;Hiroyuki Aihara;T. Okamoto
影响因子：
2.1
作者：
R. Vilar;A. Almeida
通讯作者：
R. Vilar;A. Almeida
DOI：
10.1016/j.msea.2005.03.108
发表时间：
2005-08
影响因子：
6.4
作者：
B. Willers;S. Eckert;U. Michel;I. Haase;G. Zouhar
通讯作者：
B. Willers;S. Eckert;U. Michel;I. Haase;G. Zouhar