Effect of alloyed Lu, Hf and Cr on the oxidation and spallation behavior of NiAl
Effect of alloyed Lu, Hf and Cr on the oxidation and spallation behavior of NiAl
复制标题
合金化Lu、Hf、Cr对NiAl氧化和剥落行为的影响
DOI：
10.1016/j.corsci.2017.07.016
复制
发表时间：
2017-09
影响因子：
8.3
通讯作者：
Ping Xiao
中科院分区：
文献类型：
--
作者：
Chunshan Zhao;Yuhua Zhou;Zhonghua Zou;Lirong Luo;Xiaofeng Zhao;Fangwei Guo;Ping Xiao
研究了Lu、Hf、Cr合金化对NiAl氧化和溅射行为的影响。虽然Lu与Hf一样对Al具有“阻挡效应”，但Lu掺杂的NiAl氧化速率明显高于Hf掺杂的NiAl，这是由于：（1）在氧化初期阻碍了θ-向α-Al 2 O3的转变;（2）更强的尺度晶粒细化效应和氧传输速率。S和C的偏聚不仅发生在合金/氧化膜界面处，而且发生在氧化膜内部。Lu和Hf均能显著提高氧化膜的粘附性。然而，这种有益的效果可以容易地被Cr过度补偿。
The influences of alloyed Lu, Hf and Cr on the oxidation and spallation behavior of NiAl were investigated. Although Lu has a “block effect” of Al as Hf does, the oxidation rate of Lu-doped NiAl is significantly higher, due to: (1) inhibitation of θ- to α-Al2O3transformation in early oxidation stage; (2) stronger scale grain refinement effect and enhanced oxygen transport rate. Segregation of S and C occurs not only at the alloy/scale interface, but also within the scale. Both Lu and Hf can significantly improve the scale adherence. However, This beneficial effect can be easily overcompensated by Cr.
登录
查看更多内容
影响因子：
2.1
作者：
Z. Weiss;K. Marshall
通讯作者：
Z. Weiss;K. Marshall
Cr和Si对少量Dy掺杂NiAl合金高温氧化行为的影响
影响因子：
8.3
作者：
Peng, Hui;Zhang, Yanli;Zhang, Tian;Gong, Sengkai
通讯作者：
Gong, Sengkai
影响因子：
9.4
作者：
R. Christensen;V. Tolpygo;D. Clarke
通讯作者：
R. Christensen;V. Tolpygo;D. Clarke
影响因子：
5.4
作者：
Hamadi, S.;Bacos, M. -P.;Marcus, P.
通讯作者：
Marcus, P.
影响因子：
2.2
作者：
PRESCOTT, R;GRAHAM, MJ
通讯作者：
GRAHAM, MJ