Magnetic microstructure and magnetic properties of spark plasma sintered NdFeB magnets
Magnetic microstructure and magnetic properties of spark plasma sintered NdFeB magnets
复制标题
放电等离子烧结NdFeB磁体的磁微观结构与磁性能
DOI：
10.1016/j.jmmm.2015.09.079
复制
发表时间：
2016-02
影响因子：
2.7
通讯作者：
Z. C. Zhong
中科院分区：
文献类型：
--
作者：
Y. L. Huang;Y. Wang;Y. H. Hou;Y. L. Wang;Y. Wu;S. C. Ma;Z. W. Liu;D. C. Zeng;Y. Tian;W. X. Xia;Z. C. Zhong
采用熔纺带材为起始材料，通过放电等离子烧结（SPS）技术制备纳米晶 NdFeB 磁体。 SPSed 磁体中形成了明显的两区结构，即粗晶区和细晶区。观察到粗晶区的多域颗粒和细晶区的交换相互作用域。由于磁畴壁钉扎效应的增强和交换解耦的增加，晶间非磁性相有利于提高矫顽力。各向同性磁体的剩余极化强度为 0.83 T，矫顽力为 1516 kA/m，最大磁能积为 118 kJ/m3。
Nanocrystalline NdFeB magnets were prepared by spark plasma sintering (SPS) technique using melt-spun ribbons as starting materials. A distinct two-zone structure with coarse grain zone and fine grain zone was formed in the SPSed magnets. Multi-domain particle in coarse grain zone and exchange interaction domain for fine grain zone were observed. Intergranular non-magnetic phase was favorable to improve the coercivity due to the enhancement of domain wall pinning effects and increased exchange-decouple. The remanent polarization of 0.83 T, coercivity of 1516 kA/m, and maximum energy product of 118 kJ/m3are obtained for an isotropic magnet.
登录
查看更多内容
放电等离子烧结和热变形纳米晶带材各向同性和各向异性 NdFeB 磁体的微观结构和性能演化
影响因子：
3.4
作者：
Liu, Z.W.;Zhu, J.;Zeng, D.C.;Huang, H.Y.;Zhong, X.C.;Gao, X.X.;Yu, H.Y.
通讯作者：
Yu, H.Y.
影响因子：
3.2
作者：
Khlopkov, K.;Gutfleisch, O.;Schultz, L.
通讯作者：
Schultz, L.
影响因子：
3.2
作者：
Shuwen Chen;Wei Liu;Zhidong Zhang;G. Gunaratne
通讯作者：
Shuwen Chen;Wei Liu;Zhidong Zhang;G. Gunaratne
影响因子：
4.4
作者：
Wenjian Mo;Lanting Zhang;A. Shan;L. Cao;Jian-sheng Wu;M. Komuro
通讯作者：
Wenjian Mo;Lanting Zhang;A. Shan;L. Cao;Jian-sheng Wu;M. Komuro
DOI：
10.1016/s0921-5093(02)00726-8
发表时间：
2003-06
影响因子：
6.4
作者：
O. Yanagisawa;H. Kuramoto;K. Matsugi;M. Komatsu
通讯作者：
O. Yanagisawa;H. Kuramoto;K. Matsugi;M. Komatsu