Oxidation behaviour of the nickel-based superalloy DZ125 hot-dipped with Al coatings doped by Si
Oxidation behaviour of the nickel-based superalloy DZ125 hot-dipped with Al coatings doped by Si
复制标题
镍基高温合金DZ125热浸镀Si掺杂Al镀层的氧化行为
DOI：
10.1016/j.corsci.2016.07.020
复制
发表时间：
2016-11
影响因子：
8.3
通讯作者：
Lu Jiansheng
中科院分区：
文献类型：
--
作者：
Zang Junjie;Song Peng;Feng Jing;Xiong Xiping;Chen Rong;Liu Guangliang;Lu Jiansheng
采用热浸镀法在DZ 125高温合金表面制备了纯Al涂层和Al-Si涂层。Al-Si涂层由于形成了更为致密的Al 2 O3层，因而比纯Al涂层具有更好的抗热氧化性能。Al-Si涂层经850 °C氩气热处理后，形成了以硅铝为基体的Ta 5Si 3和AlHfSi相。该层是循环氧化过程中氧和其他金属元素扩散的屏障，对致密Al 2 O3层的形成有重要影响。
A pure Al coating and Al-Si coating were prepared on the surface of the DZ125 superalloy by hot-dipping. The Al-Si coating provides better thermal oxidation resistance than that of the pure Al coating due to the formation of a more compact Al2O3layer. The microstructure of the Al-Si coating shows a silicon-aluminium-based layer with Ta5Si3and AlHfSi phase forms after heat treatment in argon at 850 °C. This layer is a barrier to the diffusion of oxygen and other metal elements during cyclic oxidation, which has a significant effect on the formation of the compact Al2O3layer.
登录
查看更多内容
DOI：
10.1016/s0921-5093(03)00107-2
发表时间：
2003-09
影响因子：
6.4
作者：
Z. Xiang;P. K. Datta
通讯作者：
Z. Xiang;P. K. Datta
影响因子：
4
作者：
Jianwei Liang;X. Ai;Z. Wen;Z. Yue
通讯作者：
Jianwei Liang;X. Ai;Z. Wen;Z. Yue
影响因子：
8.4
作者：
F. Latief;K. Kakehi
通讯作者：
F. Latief;K. Kakehi
DOI：
10.1016/0921-5093(92)90256-z
发表时间：
1992-05
影响因子：
6.4
作者：
K. Maki;M. Shioda;Mamoru Sayashi;T. Shimizu;S. Isobe
通讯作者：
K. Maki;M. Shioda;Mamoru Sayashi;T. Shimizu;S. Isobe
影响因子：
8.3
作者：
Y. Zhou;L. Wang;Guan Wang;Dongliang Jin;Hao Wei;Xiaofeng Zhao;Jian Zhang;P. Xiao
通讯作者：
Y. Zhou;L. Wang;Guan Wang;Dongliang Jin;Hao Wei;Xiaofeng Zhao;Jian Zhang;P. Xiao