Effect of annealing treatment on the structure and properties of the nanograined TiN coatings produced by ultrasonic-based coating process
Effect of annealing treatment on the structure and properties of the nanograined TiN coatings produced by ultrasonic-based coating process
复制标题
DOI：
10.1016/j.jallcom.2009.10.170
复制
发表时间：
2010-04
影响因子：
6.2
通讯作者：
S. Romankov;Y. Hayasaka;N. Hayashi;E. Kasai;S. Komarov
中科院分区：
文献类型：
--
作者：
S. Romankov;Y. Hayasaka;N. Hayashi;E. Kasai;S. Komarov
An ultrasonic mechanical coating and armouring (UMCA) process was used for the deposition of the nanograined TiN coatings. During the UMCA process, the substrate surface was subjected to high-energy ball impacts. The repeated substrate-to-ball collisions made the precoated TiN particles cold weld to each other and to the substrate. The UMCA method allows nanograined TiN coatings to be produced on different substrates in a short time at room temperature in an ambient atmosphere. Under the applied compressive loading, the substrate became strongly deformed. The grain refinement occurred and many randomly orientated nanosized grains developed near the substrate surface. Annealing treatment in temperatures ranging between 200°C and 600°C improved adhesion of the coatings and increased hardness. The nanoparticles had a tendency to consolidate with increasing annealing temperature. The growth of crystallites started at 400°C. After annealing at 600°C, a solid state reaction between Al and TiN leads to the formation of a new phase that could be intermetallic compound AlTi3.