使富含Mg和Al的模拟Magnox玻璃在静态模式下用去离子水在90 °C下经受水腐蚀7天，并使用Cameca和Ion-ToF二次离子质谱法（西姆斯）进行评估。对未沥滤和沥滤样品进行深度剖析和离子成像，以揭示从玻璃表面到本体的元素分布。对于未浸出的玻璃，所有元素均匀分布。浸出后，碱金属离子，即Na和Li的消耗被观察到，表明浸出的初始阶段的相互扩散（离子交换）过程。Mg在表面附近的富集表明富Mg晶体在近表面区域的沉淀。
A simulated Magnox glass which is Mg- and Al- rich was subjected to aqueous corrosion in static mode with deionised water at 90 °C for 7 days and assessed using Cameca and Ion-ToF Secondary Ion Mass Spectrometry (SIMS). Depth profiling and ion imaging were done for both unleached and leached samples to reveal elemental distributions from the glass surface into the bulk. All the elements were distributed evenly for unleached glass. After leaching, depletion of alkali ions i.e. Na and Li was observed indicating the interdiffusion (ion exchange) process of the initial stage of leaching. Enrichment of Mg near the surface layer indicated precipitation of Mg-rich crystals at the near surface region.
登录
查看更多内容
使用氚示踪、β-放射自显影、扫描电子显微镜和离子束分析研究碱硼硅酸盐玻璃的耐久性
DOI：
--
发表时间：
2004
期刊：
影响因子：
--
作者：
J. Chêne;P. Trocellier
通讯作者：
P. Trocellier
高放玻璃在富含各种金属阳离子的水溶液中的短期腐蚀
DOI：
--
发表时间：
2004
期刊：
影响因子：
--
作者：
B. Luckscheiter;M. Nesovic
通讯作者：
M. Nesovic
两种高放废玻璃埋入粘土后浸出层中元素的深度分布；
DOI：
--
发表时间：
2001
期刊：
影响因子：
--
作者：
A. Lodding;P. Iseghem
通讯作者：
P. Iseghem
博物馆玻璃腐蚀的 TOF-SIMS 分析
DOI：
--
发表时间：
2006
期刊：
影响因子：
--
作者：
S. Fearn;D. Mcphail;B. Hagenhoff;E. Tallarek
通讯作者：
E. Tallarek
影响因子：
2.1
作者：
Corkhill, Claire L.;Cassingham, Nathan J.;Hyatt, Neil C.
通讯作者：
Hyatt, Neil C.