Effect of anneal pre-treatment of polycrystalline aluminum sheets on synthesis of highly-ordered anodic aluminum oxide membranes
Effect of anneal pre-treatment of polycrystalline aluminum sheets on synthesis of highly-ordered anodic aluminum oxide membranes
复制标题
多晶铝片退火预处理对高有序阳极氧化铝膜合成的影响
DOI：
10.1007/s11431-008-0117-6
复制
发表时间：
2008-09
期刊：
影响因子：
--
通讯作者：
Zhang Xiao
中科院分区：
文献类型：
--
作者：
Zhang Lu;Pan CaoFeng;Zhu Jing;Zhang Xiao
采用多晶铝片退火预处理，成功制备出具有大有序孔域的阳极氧化铝（AAO）膜。引入高斯分布的统计方法来定量研究有序孔域的尺寸。有序孔域的最大平均面积为2.6μm2±0.11μm2。相应的 AAO 膜是由铝片在 893 K 退火 24 小时合成的。
Anodic aluminum oxide (AAO) membranes with large ordered pore domains were successfully prepared by adopting the anneal pre-treatment of polycrystalline aluminum sheets. A statistical method with Gaussian distribution was introduced to quantitatively study the size of the domain with ordered pores. The largest average area of ordered pore domains was 2.6 μm2±0.11 μm2. The corresponding AAO membrane was synthesized by aluminum sheets annealed at 893 K for 24 h.
登录
查看更多内容
DOI：
10.1007/pl00021073
发表时间：
2000-06
期刊：
Applied Physics A
影响因子：
--
作者：
S. Pan;D. Zeng;H. L. Zhang;H. L. Li
通讯作者：
S. Pan;D. Zeng;H. L. Zhang;H. L. Li
影响因子：
4
作者：
Jessensky, O;Muller, F;Gosele, U
通讯作者：
Gosele, U
影响因子：
3.5
作者：
Zhang Lu;Pan Cao-Feng;Zhu Jing
通讯作者：
Zhang Lu;Pan Cao-Feng;Zhu Jing
DOI：
10.1021/jp051314h
发表时间：
2005-08
期刊：
The journal of physical chemistry. B
影响因子：
--
作者：
F. Tian;J. Zhu;D. Wei;Y. Shen
通讯作者：
F. Tian;J. Zhu;D. Wei;Y. Shen
影响因子：
3.5
作者：
Lu Zhang;Caofeng Pan;Jing Zhu;Cheng Wang
通讯作者：
Lu Zhang;Caofeng Pan;Jing Zhu;Cheng Wang