Cobalt molybdate nanoflake-assembling porous pillar array for high performance pseudocapacitor
Cobalt molybdate nanoflake-assembling porous pillar array for high performance pseudocapacitor
复制标题
用于高性能赝电容器的钼酸钴纳米片组装多孔柱阵列
DOI：
10.1016/j.matlet.2015.11.011
复制
发表时间：
2016-02
影响因子：
3
通讯作者：
S. Y. Guo
中科院分区：
文献类型：
--
作者：
Z. Rong;Y. B. Chen;H. L. Zhu;S. Y. Guo
采用水热法在泡沫镍基体上制备了CoMoO4纳米片组装多孔柱阵列。XRD、SEM和TEM分析表明，CoMoO4纳米片呈花瓣状交叉堆叠形成多孔柱。作为超级电容器电极材料，CoMoO4纳米片组装多孔柱阵列表现出两对氧化还原循环伏安峰，充放电曲线也是非线性的。这表明其赝电容性质。在4 mA cm−2下获得的最大面积比电容为1.92 F cm− 2。恒电流循环试验和倍率试验表明，该材料具有良好的循环稳定性和倍率性能。
CoMoO4nanoflake-assembling porous pillar array is synthesized on Ni foam by a facile hydrothermal method. XRD, SEM and TEM demonstrate that CoMoO4nanoflakes like flower petals cross and stack to form the porous pillar. As electrode materials of supercapacitors, CoMoO4nanoflake-assembling porous pillar array show two pair of redox CV peaks, and the charging-discharging curves are also non-linear. This suggests its pseudocapacitance nature. A maximum areal specific capacitance of 1.92 F cm−2is obtained at 4 mA cm−2. The galvanostatic cycling test and rate test reveal good cycling stability and rate capability.
登录
查看更多内容
用于超级电容器的泡沫镍上 3D NiO@CoMoO4 纳米复合材料的简便制造和完美循环稳定性
影响因子：
3.9
作者：
Zhang, Wei-Bin;Liu, Mao-Cheng;Luo, Yong-Chun;Kang, Long
通讯作者：
Kang, Long
影响因子：
16.6
作者：
Mai, Li-Qiang;Yang, Fan;Luo, Yan-Zhu
通讯作者：
Luo, Yan-Zhu
影响因子：
6.6
作者：
Cheng, J. P.;Fang, J. H.;Zhang, X. B.
通讯作者：
Zhang, X. B.
影响因子：
29.4
作者：
Yu, Xinzhi;Lu, Bingan;Xu, Zhi
通讯作者：
Xu, Zhi
一步合成具有增强超级电容器电化学性能的CoMoO4/石墨烯复合材料
影响因子：
6.6
作者：
Xia, Xifeng;Lei, Wu;Wang, Xin
通讯作者：
Wang, Xin