Thermo-Analytical Investigation of Phase Equilibria in the Al2O3-SiO2 System
Thermo-Analytical Investigation of Phase Equilibria in the Al2O3-SiO2 System
复制标题
Al2O3-SiO2 体系相平衡的热分析研究
DOI：
10.1246/bcsj.40.972
复制
发表时间：
1967
影响因子：
4
通讯作者：
Senzo Kuwabara
中科院分区：
文献类型：
--
作者：
T. Horibe;Senzo Kuwabara
The phase equilibrium relation of the Al2O3-SiO2 system was thermo-analytically investigated using a molybdenum resistance furnace with an argon atmosphere and a tungsten-tungsten 26% rhenium thermocouple (supplementary experiments were also made), and the phase diargam for the high aluminous region was presented. The composition of mullite with the highest melting point is 2Al2O3·SiO2 or very close to that value, and the mullite of the composition melts in-congruently at 1890±5°C, giving a liquid with a composition slightly less in Al2O3 content than that of the mullite. Other investigators’ results were interpreted on the basis of the results of the present investigation. In the present experiment an “unstable” growth of corundum was frequently observed.