Preparation of ZrB2 based composites by reactive melt infiltration at relative low temperature
Preparation of ZrB2 based composites by reactive melt infiltration at relative low temperature
复制标题
低温反应熔渗制备ZrB2基复合材料
DOI：
10.1016/j.matlet.2011.06.070
复制
发表时间：
2011-10
影响因子：
3
通讯作者：
王松
中科院分区：
文献类型：
--
作者：
王松
采用新型反应熔体渗透工艺制备了 ZrB2 基复合材料。多孔硼棒用作预制件并被低熔点Zr2Cu金属间化合物渗透。热力学计算表明，B可以在低至1100℃的温度下与液态Zr2Cu反应形成ZrB2。通过将两种材料在真空中加热至 1200°C 3 小时来制备复合材料。利用 XRD 和 SEM 对所得复合材料进行了研究。经鉴定，ZrB2 是主要成分。复合材料的弯曲强度为414.3MPa，弯曲模量为183.6GPa，断裂韧性为5.5MPam1/2。
ZrB2based composites were prepared by a novel reactive melt infiltration process. The porous boron bars were used as preforms and infiltrated by the low melting Zr2Cu intermetallic compound. Thermodynamics calculations revealed that B could react with liquid Zr2Cu to form ZrB2as low as 1100°C. Composites were prepared by heating the two materials to 1200°C for 3h in vacuum. The resultant composites were studied with XRD and SEM. ZrB2was identified to be the main constituent. The composites had a flexural strength of 414.3MPa, a flexural modulus of 183.6GPa, and a fracture toughness of 5.5MPam1/2.
登录
查看更多内容
影响因子：
5.7
作者：
T. Zhu;Lin Xu;Xinghong Zhang;W. Han;P. Hu;L. Weng
通讯作者：
T. Zhu;Lin Xu;Xinghong Zhang;W. Han;P. Hu;L. Weng
影响因子：
3
作者：
Chen-Nan Sun;T. Baldridge;M. Gupta
通讯作者：
Chen-Nan Sun;T. Baldridge;M. Gupta
影响因子：
4.5
作者：
S. Woo;C. Kim;E. Kang
通讯作者：
S. Woo;C. Kim;E. Kang
影响因子：
--
作者：
K. Upadhya;J. Yang;W. Hoffman
通讯作者：
K. Upadhya;J. Yang;W. Hoffman
影响因子：
5.7
作者：
Linhua Zou;N. Wali;Jenn‐Ming Yang;N. Bansal
通讯作者：
Linhua Zou;N. Wali;Jenn‐Ming Yang;N. Bansal