Role of tunneling layer in graphene-oxide based organic nonvolatile memory transistors
Role of tunneling layer in graphene-oxide based organic nonvolatile memory transistors
复制标题
DOI：
10.1016/j.orgel.2012.08.020
复制
发表时间：
2012-12
影响因子：
3.2
通讯作者：
Y. Park;D. Gupta;Changhee Lee;Yongtaek Hong
中科院分区：
文献类型：
--
作者：
Y. Park;D. Gupta;Changhee Lee;Yongtaek Hong
This paper demonstrates non-volatile memory transistor using solution processable graphene oxide (GO) as charge storage nodes in the configuration, p++Si/SiO2/GO/Tunneling layer/Pentacene/Au. The tunneling layers are polymethylmethacrylate (PMMA) and polyvinylphenol (PVP). GO film could be deposited as single layered flakes with a uniform distribution using spin coating technique. The devices with PMMA as charge tunneling layer exhibited higher mobility and on/off ratio than PVP based devices. The devices show a large positive threshold voltage shift (∼24V for PMMA and ∼15V for PVP) from initial value during programming at gate voltage of +80V kept for 10s. The transfer curves can be restored approximately to its initial condition by applying an erasing voltage of −30V for 10s for both the devices. Since such a large shift is not observed without GO layer, we consider that memory effect was due to electron trapping in GO. Further, retention of the initial memory window was measured to be 63% and 37% after 3000s for PMMA and PVP based devices, respectively.