Nickel-cobalt bimetallic anode catalysts for direct urea fuel cell.
Nickel-cobalt bimetallic anode catalysts for direct urea fuel cell.
复制标题
直接尿素燃料电池用镍钴双金属阳极催化剂。
DOI：
10.1038/srep05863
复制
发表时间：
2014-08-29
影响因子：
4.6
通讯作者：
Wu Z
中科院分区：
文献类型：
--
作者：
Xu W;Zhang H;Li G;Wu Z
镍具有较高的活性，是直接尿素燃料电池（DUFC）理想的非贵金属阳极催化剂。但尿素的电氧化存在较大的过电位。本文中，制备了具有不同Co含量（0、10、20、30和40wt%）的NiCo/C纳米颗粒以提高活性。 在60°C、0.33 M尿素为燃料、O2为氧化剂的条件下，最佳Co含量为10%，最大功率密度为1.57 mW cm-2。 研究了温度和尿素浓度对DUFC性能的影响。此外，直接尿燃料电池在60°C时的最大功率密度为0.19 mW cm−2，开路电压为0.38 V。
Nickel is an ideal non-noble metal anode catalyst for direct urea fuel cell (DUFC) due to its high activity. However, there exists a large overpotential toward urea electrooxidation. Herein, NiCo/C bimetallic nanoparticles were prepared with various Co contents (0, 10, 20, 30 and 40 wt%) to improve the activity. The best Co ratio was 10% in the aspect of cell performance, with a maximum power density of 1.57 mW cm−2 when 0.33 M urea was used as fuel, O2 as oxidant at 60°C. The effects of temperature and urea concentration on DUFC performance were investigated. Besides, direct urine fuel cell reaches a maximum power density of 0.19 mW cm−2 with an open circuit voltage of 0.38 V at 60°C.
登录
查看更多内容
影响因子：
1
作者：
Gojkovic, SL
通讯作者：
Gojkovic, SL
影响因子：
3.9
作者：
Kim, JW;Park, SM
通讯作者：
Park, SM
PdCo双金属纳米空心球对甲酸氧化的电催化性能
影响因子：
2.5
作者：
Tang, Yawen;Chen, Yu;Lu, Tianhong
通讯作者：
Lu, Tianhong
影响因子：
4.6
作者：
Hwang, Seung Jun;Yoo, Sung Jong;Shin, Jungho;Cho, Yong-Hun;Jang, Jong Hyun;Cho, Eunae;Sung, Yung-Eun;Nam, Suk Woo;Lim, Tae-Hoon;Lee, Seung-Cheol;Kim, Soo-Kil
通讯作者：
Kim, Soo-Kil
影响因子：
6.7
作者：
Dai, WL;Qiao, MH;Deng, JF
通讯作者：
Deng, JF