Corrosion protection of aluminium alloy 2024-T3 in 0.05 M NaCl by cerium cinnamate
Corrosion protection of aluminium alloy 2024-T3 in 0.05 M NaCl by cerium cinnamate
复制标题
肉桂酸铈对铝合金 2024-T3 在 0.05 M NaCl 中的腐蚀防护
DOI：
10.1016/j.corsci.2011.03.012
复制
发表时间：
2011-07
影响因子：
8.3
通讯作者：
Liu, Fuchun
中科院分区：
文献类型：
--
作者：
Shi, Hongwei;Han, En-Hou;Liu, Fuchun
研究了肉桂酸铈对 AA 2024-T3 在 0.05 M NaCl 中的腐蚀防护作用。极化测量表明，肉桂酸铈在最初 72 小时的浸泡过程中对于抑制合金腐蚀的阳极过程非常有效。浸泡期间的保护机制似乎涉及两个阶段：肉桂酸铈的沉积，然后铈离子的水解形成氧化铈/氢氧化铈，优于前述沉积。本研究还通过 X 射线光电子能谱和电子探针微分析阐明了肉桂酸铈对第二相颗粒发生的早期腐蚀的抑制作用。
The corrosion protection of AA 2024-T3 in 0.05 M NaCl by cerium cinnamate has been studied. Polarization measurements demonstrate that cerium cinnamate is markedly effective for suppressing anodic process of the alloy corrosion during the initial 72 h of immersion. The protection mechanism during the immersion period appears to involve two stages: the deposition of cerium cinnamate, and then hydrolysis of cerium ions forming a cerium oxide/hydroxide, prevailing over the foregoing deposition. This study also elucidates the inhibition effect of cerium cinnamate on the early corrosion attack occurred from the second phase particles by X-ray photoelectron spectroscopy and electron-probe microanalysis.
登录
查看更多内容
DOI：
--
发表时间：
2009-10
期刊：
--
影响因子：
--
作者：
Y.L.Cheng;J.F.Li;J.Q.Zhang;C.N.Cao;F.H.Cao;Z.Zhanq
通讯作者：
Y.L.Cheng;J.F.Li;J.Q.Zhang;C.N.Cao;F.H.Cao;Z.Zhanq
影响因子：
6.6
作者：
K. Rahmouni;N. Hajjaji;M. Keddam;A. Srhiri;H. Takenouti
通讯作者：
K. Rahmouni;N. Hajjaji;M. Keddam;A. Srhiri;H. Takenouti
影响因子：
3.9
作者：
Lin Xia;E. Akiyama;G. Frankel;R. McCreery
通讯作者：
Lin Xia;E. Akiyama;G. Frankel;R. McCreery
影响因子：
3.9
作者：
Jun Zhao;G. Frankel;R. McCreery
通讯作者：
Jun Zhao;G. Frankel;R. McCreery
影响因子：
3.9
作者：
Aldykiewicz, AJ;Davenport, AJ;Isaacs, HS
通讯作者：
Isaacs, HS