Long-term oxidation behaviors of C/SiC composites with a SiC/UHTC/SiC three-layer coating in a wide temperature range
Long-term oxidation behaviors of C/SiC composites with a SiC/UHTC/SiC three-layer coating in a wide temperature range
复制标题
SiC/UHTC/SiC三层涂层C/SiC复合材料在宽温度范围内的长期氧化行为
DOI：
10.1016/j.corsci.2018.10.017
复制
发表时间：
2019-02
影响因子：
8.3
通讯作者：
Hui-Ming Cheng
中科院分区：
文献类型：
--
作者：
Chenglong Hu;Sufang Tang;Shengyang Pang;Hui-Ming Cheng
采用化学气相沉积和电刷烧结技术，设计了SiC/UHTC/SiC三层涂层，并在C/SiC复合材料表面进行了涂覆，实现了在大温度范围内的长期氧化保护。在1100°C和1300°C的空气中暴露114小时和1500°C的空气中暴露68小时后，涂层复合材料的质量损失分别仅为0.36、1.65和3.45 mg/cm2。zrb2基超高温陶瓷层（UHTC）与SiC层的协同作用可显著降低材料的质量损失率。详细讨论了不同温度下的氧化过程和保护机理。
A SiC/UHTC/SiC triple layer was designed and coated on C/SiC composites by chemical vapor deposition and brushing-sintering techniques to achieve long-term oxidation protection in a wide temperature range. After exposure to 1100 °C and 1300 °C for 114 h, and 1500 °C for 68 h in air, the coated composites exhibited mass losses of only 0.36, 1.65 and 3.45 mg/cm2, respectively. The low mass loss rates can be attributed to the synergistic effects of the ZrB2-based ultra-high temperature ceramic (UHTC) and SiC layers. The oxidation process and protective mechanism at different temperatures were discussed in detail.
登录
查看更多内容
影响因子：
5.2
作者：
Y. Xiang;Wei Li;Song Wang;Zhaohui Chen
通讯作者：
Y. Xiang;Wei Li;Song Wang;Zhaohui Chen
氧乙炔火炬环境下SiC涂层C/C复合材料HfC-HfO2保护涂层的烧蚀机理
影响因子：
10.9
作者：
Yang Yang;Li Kezhi;Liu Guanxi;Zhao Zhigang;Li KZ
通讯作者：
Li KZ
磷酸盐涂层对C/C和C/SiC制动材料摩擦性能的影响
影响因子：
6.2
作者：
Shangwu Fan;Chuan Yang;Liuyang He;Juanli Deng;Litong Zhang;Laifei Cheng
通讯作者：
Laifei Cheng
影响因子：
4.5
作者：
M. Westwood;James D. Webster;Richard J. Day;F. Hayes;R. Taylor
通讯作者：
M. Westwood;James D. Webster;Richard J. Day;F. Hayes;R. Taylor
影响因子：
6
作者：
Fu, QG;Li, HJ;Sun, GD
通讯作者：
Sun, GD