Crystallization behavior and hydrogen storage kinetics of amorphous Mg11Y2Ni2 alloy
Crystallization behavior and hydrogen storage kinetics of amorphous Mg11Y2Ni2 alloy
复制标题
非晶Mg11Y2Ni2合金的结晶行为及储氢动力学
DOI：
10.1016/j.jallcom.2012.11.046
复制
发表时间：
2013-02
影响因子：
6.2
通讯作者：
Q.A. Zhang, L.X. Zhang, Q.Q. Wang
中科院分区：
文献类型：
--
作者：
Q.A. Zhang, L.X. Zhang, Q.Q. Wang
研究了快淬法制备的Mg 11 Y2 Ni 2非晶合金的晶化行为和储氢动力学。结果表明，非晶态Mg 11 Y2 Ni 2合金在279°C时转变为亚稳态的晶态Mg 11 Y2 Ni 2，在366°C时分解为Mg、YMgNi 4和Y（Mg）固溶体。非晶、亚稳和稳定的Mg_（11）Y_（2Ni）_2合金均能被氢化成MgH_2、Mg_2Ni_（H4）和YH_2/YH_3。但由于YH 2/YH 3和Mg 2NiH 4的分散性较差，稳定的Mg 11 Y2 Ni 2合金吸放氢动力学稍慢。
The crystallization behavior and hydrogen storage kinetics of the amorphous Mg11Y2Ni2alloy prepared by melt-spinning technique were investigated in detail. It was found that the amorphous Mg11Y2Ni2alloy transforms into the crystalline Mg11Y2Ni2in metastable state at 279°C and subsequently decomposes into Mg, YMgNi4and Y(Mg) solid solution in stable state at 366°C. All the amorphous, metastable and stable Mg11Y2Ni2alloys can be hydrogenated into MgH2, Mg2NiH4and YH2/YH3. However, the stable Mg11Y2Ni2alloy has slightly slower hydrogen absorption–desorption kinetics due to the worse dispersivity of YH2/YH3and Mg2NiH4.
登录
查看更多内容
影响因子：
6.2
作者：
Amira, S.;Huot, J.
通讯作者：
Huot, J.
影响因子：
6.2
作者：
S. Kalinichenka;L. Röntzsch;C. Baehtz;T. Weissgärber;B. Kieback
通讯作者：
S. Kalinichenka;L. Röntzsch;C. Baehtz;T. Weissgärber;B. Kieback
DOI：
10.1016/j.msea.2006.05.011
发表时间：
2006-07
影响因子：
6.4
作者：
Da-quan Li;Qudong Wang;W. Ding
通讯作者：
Da-quan Li;Qudong Wang;W. Ding
影响因子：
6.2
作者：
J. Zhang;Yangqiang Huang;C. Mao;P. Peng
通讯作者：
J. Zhang;Yangqiang Huang;C. Mao;P. Peng
影响因子：
6.2
作者：
Ouyang, L. Z.;Dong, H. W.;Zhu, M.
通讯作者：
Zhu, M.