Mechanically driven phase separation and corresponding microhardness change in Cu60Zr20Ti20 bulk metallic glass
Mechanically driven phase separation and corresponding microhardness change in Cu60Zr20Ti20 bulk metallic glass
复制标题
Cu60Zr20Ti20 大块金属玻璃中机械驱动的相分离和相应的显微硬度变化
DOI：
10.1063/1.1862329
复制
发表时间：
2005-02
影响因子：
4
通讯作者：
Jianzhong Jiang
中科院分区：
文献类型：
--
作者：
Qingping Cao;Jinfu Li;Yaohe Zhou;Jianzhong Jiang
对Cu60Zr20Ti20块体非晶合金进行了低温轧制变形。试样表现出良好的延展性，并被轧制到97%的厚度减少没有断裂。在变形过程中结晶被抑制，然而，当厚度减少超过89%时，在玻璃基质中观察到相分离。一旦发生相分离，试样的显微硬度急剧增加，表明存在由金属玻璃的剧烈塑性变形引起的加工硬化。
Rolling deformation of bulk Cu60Zr20Ti20 metallic glass has been performed at cryogenic temperature. The specimens exhibit excellent ductility, and are rolled up to 97% reduction in thickness without fracture. Crystallization is suppressed during the deformation, however, phase separation is observed in the glassy matrix when the thickness reduction exceeds 89%. Once the phase separation occurs, the microhardness of the specimen increases drastically, indicating the existence of work hardening by severe plastic deformation of the metallic glass.
登录
查看更多内容
DOI：
10.1016/0001-6160(79)90055-5
发表时间：
1979-01-01
期刊：
ACTA METALLURGICA
影响因子：
--
作者：
ARGON, AS
通讯作者：
ARGON, AS
DOI：
10.1007/s11661-998-0004-6
发表时间：
1998-07-01
影响因子：
2.8
作者：
Liu, CT;Heatherly, L;Inoue, A
通讯作者：
Inoue, A
DOI：
10.1016/s0022-5096(01)00115-6
发表时间：
2002-05-01
影响因子：
5.3
作者：
Huang, R;Suo, Z;Nix, WD
通讯作者：
Nix, WD
影响因子：
9.4
作者：
Jae-Chul Lee;Yu-Chan Kim;Jae-pyoung Ahn;Hyoung-Seop Kim;Sunghak Lee;Byeong-Joo Lee
通讯作者：
Jae-Chul Lee;Yu-Chan Kim;Jae-pyoung Ahn;Hyoung-Seop Kim;Sunghak Lee;Byeong-Joo Lee
影响因子：
4
作者：
M. Trudeau
通讯作者：
M. Trudeau