Bonding Interface and Bending Deformation of Al/316LSS Clad Metal Prepared by Explosive Welding
Bonding Interface and Bending Deformation of Al/316LSS Clad Metal Prepared by Explosive Welding
复制标题
爆炸焊接Al/316LSS复合金属的结合界面及弯曲变形
DOI：
10.1007/s11665-016-2057-9
复制
发表时间：
2016-04
影响因子：
2.3
通讯作者：
Fuye Ma
中科院分区：
文献类型：
--
作者：
Xunzhong Guo;Minyu Fan;Liuan Wang;Fuye Ma
采用SEM、EDS、XRD等分析手段，对爆炸焊接Al/316LSS复合材料的界面形貌、元素分布和相组成进行了研究，并对爆炸焊接Al/316LSS复合材料的界面结合性能进行了评价。此外，还研究了其显微硬度和弯曲性能。结果表明，界面呈波浪形和线状共存，局部存在金属间化合物相。此外，在连接界面处的金属间化合物相的显微硬度值高于在界面处没有任何金属间化合物相。此外，在弯曲成形过程中，块状金属化合物容易导致微裂纹的产生。
The morphology, elemental distribution, and phase analysis of the bonding interface were investigated by means of SEM, EDS, and XRD to evaluate the interface bonding properties of Al/316LSS clad metal prepared by explosive welding method. Furthermore, the micro-hardness and bending properties were also investigated. The results indicated that the linear and wavy bonding interfaces coexisted and intermetallic phases were present in the local interfacial zone. Moreover, the micro-hardness value at the bonding interface with intermetallic phases was higher than that at the interface without any intermetallic phases. In addition, bulk metal compounds could easily lead to the generation of micro-cracks during the bending forming process.
登录
查看更多内容
影响因子：
8.3
作者：
Xiaoxu Ma;Yedong He;Deren Wang;Jin Zhang
通讯作者：
Xiaoxu Ma;Yedong He;Deren Wang;Jin Zhang
影响因子：
6.3
作者：
A. Almathami;M. Brochu
通讯作者：
A. Almathami;M. Brochu
DOI：
--
发表时间：
2013
期刊：
--
影响因子：
--
作者：
M. Konieczny
通讯作者：
M. Konieczny
DOI：
10.1007/bf03025984
发表时间：
1998-11
期刊：
Metals and Materials
影响因子：
--
作者：
J. Evans;D. Xu;W. Jones
通讯作者：
J. Evans;D. Xu;W. Jones
影响因子：
4.7
作者：
Yanbo Sun;J. Chen;Ma Fengmei;K. Ameyama;W. Xiao;Chao-Li Ma
通讯作者：
Yanbo Sun;J. Chen;Ma Fengmei;K. Ameyama;W. Xiao;Chao-Li Ma