Possible High TQ in YbAl3C3 with 4 f13 System
Possible High TQ in YbAl3C3 with 4 f13 System
复制标题
采用 4 f13 系统的 YbAl3C3 可能具有高 TQ
DOI：
10.1143/jpsj.74.2413
复制
发表时间：
2005
影响因子：
1.7
通讯作者：
S. Tozer
中科院分区：
文献类型：
--
作者：
M. Kosaka;Y. Kato;Chieko Araki;N. Mōri;Y. Nakanishi;M. Yoshizawa;K. Ohoyama;Catalin Martin;S. Tozer
报道了YbAl3C3的四极有序[Tq]的最高转变温度，在该温度范围内，用比热和超声测量观察到明显的反常，磁化强度只有很小的变化，用中子衍射测量没有观察到磁性或结构相变。因此，我们认为YbAl3C3具有迄今发现的最高T_q的反铁四极有序，并首次实现了稀土金属间化合物和金属间化合物的这种超越液氮温度的有序。
We report the highest transition temperature of quadrupolar ordering [ T Q ] in YbAl 3 C 3 , where a distinct anomaly is observed by specific heat and ultrasonic measurements at 80 K. Magnetization measurements show only a very slight change and no magnetic or structural phase transitions can be observed by neutron diffraction measurements in this temperature range. Therefore, we believe that YbAl 3 C 3 shows an antiferroquadrupolar ordering with the highest T Q found to date and is the first realization of this ordering beyond liquid nitrogen temperatures for rare-earth and actinide intermetallic compounds.
隧道二极管振荡器在脉冲磁场非接触电阻率测量中的应用
DOI：
--
发表时间：
2004
期刊：
Rev.Sci.Inst. 75
影响因子：
--
作者：
H. Wada;T. Mori;Takao Someya;E.Ohmichi
通讯作者：
E.Ohmichi