Tween20 surfactant effect on the electrocatalytic performance of porous carbon micro-spheres supported MnO2
Tween20 surfactant effect on the electrocatalytic performance of porous carbon micro-spheres supported MnO2
复制标题
Tween20表面活性剂对多孔碳微球负载MnO2电催化性能的影响
DOI：
10.1039/c4ra09169h
复制
发表时间：
2014-10
期刊：
影响因子：
3.9
通讯作者：
Wang Hong-Qiang
中科院分区：
文献类型：
--
作者：
Li Qing-Yu;Wu Yong-Sheng;Zhang Xiao-Hui;Huang You-Guo;Wu Qiang;Wang Hong-Qiang
研究了聚氧乙烯失水山梨醇单月桂酸酯（Tween 20）修饰的多孔碳微球（PCS）负载的MnO 2催化剂在0.1M KOH溶液中的电催化析氧性能。Super P（SP）的加入提高了催化剂的电导率。电化学测试结果表明，Tween 20修饰后MnO 2/PCS对析氧反应的电催化活性显著增强。Tween 20修饰的MnO 2/PCS颗粒电极的OER的起始电位比裸（即未修饰的）MnO 2/PCS电极更负约0.162 V。Tween 20吸附在MnO 2/PCS颗粒表面，均匀地覆盖了整个MnO 2/PCS颗粒表面。Tween 20作为催化介体起着至关重要的作用，其在水氧化成分子氧期间促进离子转移，从而在较小的正电位下实现OER。
This study is concerned with the electrocatalytic evolution of oxygen at polyoxyethylene sorbitan monolaurate (Tween20) modified porous carbon micro-spheres (PCS) supported MnO2 catalyst in 0.1 M KOH solution. The Super P (SP) was used to improve the electrical conductivity of the catalyst. The electrochemical measurements revealed a significant enhancement of the electrocatalytic activity of the MnO2/PCS towards the oxygen evolution reaction (OER) upon the Tween20 modification. The onset potentials of the OER at the Tween20 modified MnO2/PCS particles electrode are more negative by about 0.162 V compared with the bare (i.e. unmodified) MnO2/PCS electrode. Tween20 is absorbed on the surface of MnO2/PCS and covers the entire surface of the MnO2/PCS particles homogeneously. The Tween20 plays a vital role as a catalytic mediator, which facilitates the ion transfer during the water oxidation into molecular oxygen and thus the OER is accomplished at less positive potentials.
登录
查看更多内容
影响因子：
4.5
作者：
X. Tong;M. Aindow;J. Farr
通讯作者：
X. Tong;M. Aindow;J. Farr
影响因子：
6.6
作者：
A. Polcaro;S. Palmas
通讯作者：
A. Polcaro;S. Palmas
影响因子：
3
作者：
Zonghui Yi;Yongguang Liang;Xuefeng Lei;Chiwei Wang;Ju-tang Sun
通讯作者：
Zonghui Yi;Yongguang Liang;Xuefeng Lei;Chiwei Wang;Ju-tang Sun
影响因子：
15
作者：
Yeo, Boon Siang;Bell, Alexis T.
通讯作者：
Bell, Alexis T.
影响因子：
9.9
作者：
Dao-Jun Guo;Hu-lin Li
通讯作者：
Dao-Jun Guo;Hu-lin Li