Energy storage performance of Na0.5Bi0.5TiO3-SrTiO3 lead-free relaxors modified by AgNb0.85Ta0.15O3
Energy storage performance of Na0.5Bi0.5TiO3-SrTiO3 lead-free relaxors modified by AgNb0.85Ta0.15O3
复制标题
AgNb0.85Ta0.15O3改性Na0.5Bi0.5TiO3-SrTiO3无铅弛豫剂的储能性能
DOI：
10.1016/j.cej.2020.127151
复制
发表时间：
2021-02-15
影响因子：
15.1
通讯作者：
Wang, Chunchang
中科院分区：
文献类型：
--
作者：
Li, Tianyu;Chen, Pengfei;Wang, Chunchang
Exploring eco-friendly energy-storage ceramics simultaneously featuring large recoverable energy storage density (W-rec), high energy storage efficiency (eta), and excellent temperature/frequency stabilities is highly desirable for the applications of pulsed power systems. Herein, AgNb0.85Ta0.15O3 was used to modify Na0.5Bi0.5TiO3 based lead-free relaxor ferroelectric ceramics in an effort to enhance the breakdown electric field strength. The ceramics (1-x)(0.75Na(0.5)Bi(0.5)TiO(3)-0.25SrTiO(3))-xAg(Nb0.85Ta0.15)O-3 (x = 0, 0.05, 0.1, and 0.15) were prepared by the conventional solid-state reaction method. The microstructure, dielectric, and energy storage properties of all the ceramics have been systematically studied. Our results show that the introduction of AgNb0.85Ta0.15O3 leads to a homogeneous microstructure and small grain size, thereby increasing the strength of the dielectric breakdown field (29 kV/mm). In addition, it can also decompose the macroscopic long-range ferroelectric order into randomly-oriented polar nano-regions (PNRS), resulting in a board diffusive phase. A large W-rec (3.6 J/cm(3)) and high eta (80%) as well as excellent temperature and frequency stabilities were simultaneously achieved in the sample with x = 0.1. This work provides a feasible method for designing lead-free ceramics with high energy storage performances.