Microstructures and mechanical properties of Al2O3/ZrO2 composite produced by combustion synthesis
Microstructures and mechanical properties of Al2O3/ZrO2 composite produced by combustion synthesis
复制标题
DOI：
10.1016/j.scriptamat.2005.06.016
复制
发表时间：
2005-10
影响因子：
6
通讯作者：
Zhong Zhao;Longyu Zhang;Jian Zheng;H. Bai;Shiyue Zhang;B. Xu
中科院分区：
文献类型：
--
作者：
Zhong Zhao;Longyu Zhang;Jian Zheng;H. Bai;Shiyue Zhang;B. Xu
在铝热剂中加入ZrO2（3Y）微米粉体，利用燃烧合成法制备了ZrO2纳米微米纤维增强Al2O3基陶瓷。陶瓷的弯曲强度和断裂韧性分别为1268MPa和12.6MPa·m0.5。
By adding ZrO2(3Y) micron powder into a thermit, Al2O3matrix ceramics reinforced by ZrO2nano-micron fibers have been fabricated from the melts produced by combustion synthesis. Flexural strength and fracture toughness of the ceramics measured 1268MPa and 12.6MPa·m0.5, respectively.