Improved hot corrosion resistance of Dy-Co-modified aluminide coating by pack cementation process on nickel base superalloys
Improved hot corrosion resistance of Dy-Co-modified aluminide coating by pack cementation process on nickel base superalloys
复制标题
镍基高温合金包渗工艺提高 Dy-Co 改性铝化物涂层的热腐蚀性能
DOI：
10.1016/j.corsci.2016.09.011
复制
发表时间：
2016-11
影响因子：
8.3
通讯作者：
Chungen Zhou
中科院分区：
文献类型：
--
作者：
Pei Yuwen;Chungen Zhou
采用复合渗碳法在DZ125镍基高温合金表面制备了Dy-Co变质铝化物涂层。研究了涂层的组织结构和热腐蚀行为。结果表明，镀态涂层为双层结构。涂层外层主要由Al0.9Ni1.1和弥散分布的Dy2Hf2O7组成。涂层在900℃、75wt.%Na2SO4+25wt.%氯化钠溶液中腐蚀100h后，增重率为0.23 mg/cm2，腐蚀产物为Al_2O_3。讨论了Dy在提高耐热腐蚀性能中的作用。
Dy-Co-modified aluminide coating was deposited onto Ni-based superalloy DZ125 using pack cementation method. The microstructure and hot corrosion behavior of the coating were investigated. The results show that as-deposited coating has a two-layer structure. The outer layer of the coating is composed mainly of Al0.9Ni1.1with dispersed Dy2Hf2O7. The mass gain of the coating is 0.23 mg/cm2after exposure to 75 wt.% Na2SO4+ 25 wt.% NaCl at 900 °C for 100 h. The corrosion product formed on the coating is characterized as Al2O3. Role of Dy in the improvement of the hot corrosion resistance has been discussed.
登录
查看更多内容
影响因子：
8.3
作者：
Hui Huang;Chao Liu;L. Ni;Chungen Zhou
通讯作者：
Hui Huang;Chao Liu;L. Ni;Chungen Zhou
镍基高温合金上无 Pt 和 Pt 改性 δ-Ni2Si 涂层的显微组织和氧化行为比较
影响因子：
8.3
作者：
C. Fu;C.H. Wang;Z.M. Ren;G.H. Cao
通讯作者：
G.H. Cao
镍基高温合金上Hf-Co改性铝化物涂层的形成及其抗循环氧化性能
影响因子：
4.6
作者：
Haixia Li;Min Qiao;Chungen Zhou
通讯作者：
Chungen Zhou
影响因子：
1.7
作者：
Hongbo Guo;Xiaoyang Wang;S. Gong
通讯作者：
Hongbo Guo;Xiaoyang Wang;S. Gong
DOI：
10.1016/s0921-5093(02)00742-6
发表时间：
2003-05
影响因子：
6.4
作者：
Chungen Zhou;Jingsheng Yu;S. Gong;Huibin Xu
通讯作者：
Chungen Zhou;Jingsheng Yu;S. Gong;Huibin Xu