The effect of oxidation on the mechanical properties and dielectric properties of porous Si3N4 ceramics
The effect of oxidation on the mechanical properties and dielectric properties of porous Si3N4 ceramics
复制标题
DOI：
10.1016/j.ceramint.2017.01.074
复制
发表时间：
2017-05-01
影响因子：
5.2
通讯作者：
Yin, Jinwei
中科院分区：
文献类型：
--
作者：
Liang, Hanqin;Zeng, Yuping;Yin, Jinwei
The effect of oxidation temperature and time on the microstructures, phase compositions, mechanical properties, and dielectric properties of porous Si3N4 ceramics was investigated in the temperature range from 900 degrees C to 1300 degrees C for 1 h, 5 h, and 24 h. The weight gain measured either at lower temperature (900 degrees C) for long time (24 h) or at higher temperature (1300 degrees C) for 1 h demonstrated that the porous Si3N4 ceramics were easily oxidized under the current test conditions. Results showed that the amount of open pores, flexural strength, compressive strength, and dielectric constant all decreased with the increase of oxidation temperature independent upon the oxidation time. The oxidation product SiO2 was low-temperature quartz in mild condition (low temperature, short time) and cristobalite in severe condition (high temperature, long time). The existence of cracks on the oxide scale was due to the phase transformation of SiO2 and thermal expansion coefficient mismatch between SiO2 and Si3N4.