Phase segregation of titanium-aluminium carbide (Ti2AlC) at high pressure and high temperature
Phase segregation of titanium-aluminium carbide (Ti2AlC) at high pressure and high temperature
复制标题
高压高温下碳化钛铝（Ti2AlC）的相偏析
DOI：
10.1016/j.jallcom.2007.08.032
复制
发表时间：
2008-08
影响因子：
6.2
通讯作者：
中科院分区：
文献类型：
--
作者：
采用X射线衍射（XRD）、差示扫描量热法（DSC）、扫描电镜（SEM）和能谱分析（EDXA）等方法研究了钛铝碳化物（Ti 2AlC）的高温高压行为和相稳定性。结果表明，Ti 2AlC的分解温度随压力的增大而降低。在3、4和5GPa压力下，Ti_2Al_C相分离的低温极限分别为1300 ~ 1200 ℃、1100 ~ 1000 ℃、900 ~ 800 ℃。分解产物经鉴定为碳化钛和钛铝。
The high pressure and high temperature (HPHT) behavior and phase stability of titanium-aluminium carbide (Ti2AlC) were investigated using X-ray diffraction (XRD), differential scanning calorimetry (DSC), scanning electron micrograph (SEM), and energy-dispersive X-ray analysis (EDXA). The results show that the decomposition temperature of Ti2AlC decreases against pressure. At pressures of 3, 4 and 5GPa, the low temperature limits of phase segregation of the sample Ti2AlC lie between 1300 and 1200°C, 1100 and 1000°C, 900 and 800°C, respectively. The decomposition products are identified to be titanium carbide and titanium aluminium.
登录
查看更多内容
影响因子：
6
作者：
Barsoum, MW;Brodkin, D;ElRaghy, T
通讯作者：
ElRaghy, T
影响因子：
1.8
作者：
JEITSCHKO, W;NOWOTNY, H;BENESOVSKY, F
通讯作者：
BENESOVSKY, F
DOI：
10.1007/s11661-999-0325-0
发表时间：
1999-02-01
影响因子：
2.8
作者：
Barsoum, MW;El-Raghy, T
通讯作者：
El-Raghy, T
影响因子：
3.2
作者：
J. Jordan;T. Sekine;Takamichi Kobayashi;Xijun Li;N. Thadhani;T. El-Raghy;M. Barsoum
通讯作者：
J. Jordan;T. Sekine;Takamichi Kobayashi;Xijun Li;N. Thadhani;T. El-Raghy;M. Barsoum
影响因子：
4
作者：
B. Manoun;S. Saxena;T. El-Raghy;M. Barsoum
通讯作者：
B. Manoun;S. Saxena;T. El-Raghy;M. Barsoum