Tribological property of plasma-sprayed Al2O3-13wt%TiO2 coatings onto resin-based composites
Tribological property of plasma-sprayed Al2O3-13wt%TiO2 coatings onto resin-based composites
复制标题
摩擦学%20性能%20of%20等离子喷涂%20Al2O3-13wt%TiO2%20涂层%20onto%20树脂基%20复合材料
DOI：
10.1016/j.apsusc.2017.05.239
复制
发表时间：
2018-02
影响因子：
6.7
通讯作者：
Wang Yue
中科院分区：
文献类型：
--
作者：
Zou Zhiwei;Wang You;Zhou Feifei;Wang Liang;Liu Saiyue;Wang Yue
采用大气等离子喷涂(APS)技术在树脂基复合材料表面制备了纳米结构的Al_2O_3-13wt%TiO_2涂层。系统地研究了涂层的力学性能和摩擦学性能。结果表明，当喷涂电流为650A时，涂层的硬度和结合强度达到最佳值，在稳定磨损阶段，涂层的摩擦系数保持在0.2。喷涂电流在600~650℃时，涂层的耐磨性最好。
The nanostructured Al2O3–13 wt% TiO2coatings were fabricated by atmospheric plasma spraying (APS) on the surface of resin-based composites. The mechanical and tribological properties of coatings were investigated systematically. The results reveal that the hardness and bonding strength of the coatings reach the optimization when the spraying current is 650 A. The friction coefficient of the coatings remains at 0.2 during the steady wear stage. The wear resistance of the coatings is the highest at spraying current range from 600 A to 650 A.
登录
查看更多内容
影响因子：
5.4
作者：
O. Tingaud;P. Bertrand;G. Bertrand
通讯作者：
O. Tingaud;P. Bertrand;G. Bertrand
DOI：
--
发表时间：
2002
期刊：
S.A.M.P.E. journal
影响因子：
--
作者：
S. Connell;A. Abusafieh
通讯作者：
S. Connell;A. Abusafieh
影响因子：
5.7
作者：
Qinghe Yu;Chungen Zhou;Huiyan Zhang;F. Zhao
通讯作者：
Qinghe Yu;Chungen Zhou;Huiyan Zhang;F. Zhao
YSZ/Al2O3微叠层涂层的制备及其对MCrAlY合金抗氧化和抗剥落性能的影响
影响因子：
5.7
作者：
He, Yedong;Gao, Junguo;Wang, Deren
通讯作者：
Wang, Deren
影响因子：
3
作者：
Cheng, Qunfeng;Fang, Zhengping;Xu, Yahong
通讯作者：
Xu, Yahong