Effect of charge compensators (Li+, Na+, K+) on the luminescence properties of Sr3TeO6:Eu3+ red phosphor
Effect of charge compensators (Li+, Na+, K+) on the luminescence properties of Sr3TeO6:Eu3+ red phosphor
复制标题
DOI：
10.1016/j.ceramint.2020.11.219
复制
发表时间：
2020-12
影响因子：
5.2
通讯作者：
Yingying Ma;Shigao Chen;Junzhi Che;Jianxu Wang;Ruyi Kang;J. Zhao;Bin Deng;Ruijin Yu;
中科院分区：
文献类型：
--
作者：
Yingying Ma;Shigao Chen;Junzhi Che;Jianxu Wang;Ruyi Kang;J. Zhao;Bin Deng;Ruijin Yu;
A double-perovskite Sr3TeO6:Eu3+red phosphor was successfully prepared and confirmed to be a single phase through X-ray diffraction. Under an optimal excitation wavelength (394 nm), the Sr3TeO6:Eu3+phosphor emitted intense red light at 617 nm, which corresponded to5D0→7F2transition. When the concentration of Eu3+exceeded the optimal doping concentration (25 mol%), concentration quenching occurred because of the interactions among the nearest neighbor ions. The phosphor exhibited excellent thermal stability, and theEavalue was 0.27 eV. In accordance with Judd–Ofelt theory, the low symmetry of Eu3+ions was confirmed, and it resulted in a color purity of up to 99.5%–99.8%. Among the charge compensators (Li+, Na+, and K+), the Na+ions had the best charge compensation effect. The luminescence intensity of Sr3TeO6:Eu3+, Na+was approximately 2.06 times that of Sr3TeO6:Eu3+and 2.25 times that of commercial phosphor (Y2O3:Eu3+). The fabricated red LED has the potential to be used for plant and herb cultivation. A white light–emitting diode (w–LED) was successfully prepared, and related parameters were established. The Ravalue of the prepared w–LED was as high as 91, and R9was 5.7 times that of a commercial w–LED. These characteristics indicate that phosphors have potential in the solid-state lighting field.