Different R-Curves for Two- and Three-Dimensional Cracks
Different R-Curves for Two- and Three-Dimensional Cracks
复制标题
二维和三维裂纹的不同 R 曲线
DOI：
10.1007/s10704-008-9289-0
复制
发表时间：
2008
影响因子：
2.5
通讯作者：
R. Oberacker
中科院分区：
文献类型：
--
作者：
T. Fett;S. Fünfschilling;Michael J. Hoffmann;R. Oberacker
由裂纹面相互作用引起的R曲线对于具有小裂纹的构件的强度评估是重要的。尽管在断裂力学的基础上很好地理解了初始裂纹长度对R曲线的影响，但这里将表明，裂纹的类型也影响裂纹扩展阻力。对于一个给定的裂纹桥接关系，它可以表明，三维裂纹的圆形内部裂纹和半圆形表面裂纹必须表现出一个较低的R曲线比从二维边缘裂纹。
R-curves caused by crack face interactions are important for the strength assessment of components with small cracks. Whereas an influence of the initial crack length on the R-curve is well understood on the basis of fracture mechanics, it will be shown here that also the type of the crack affects the crack growth resistance. For a given crack-bridging relation it can be shown that 3-dimensional cracks as circular internal cracks and semi-circular surface cracks must exhibit a lower R-curve than obtainable from 2-dimensional edge cracks.
影响因子：
5.4
作者：
NEWMAN, JC;RAJU, IS
通讯作者：
RAJU, IS
Tada, H.：“感觉形态和精神负荷对眨眼率的影响。”
DOI：
--
发表时间：
--
期刊：
影响因子：
--
作者：
通讯作者：
--