Enhanced figure of merit in antimony telluride thermoelectric materials by In-Ag co-alloying for mid-temperature power generation
Enhanced figure of merit in antimony telluride thermoelectric materials by In-Ag co-alloying for mid-temperature power generation
复制标题
通过 In-Ag 共合金提高中温发电碲化锑热电材料的品质因数
DOI：
10.1016/j.actamat.2014.11.023
复制
发表时间：
2015-02-15
期刊：
影响因子：
9.4
通讯作者：
Zhao, X. B.
中科院分区：
文献类型：
--
作者：
Hu, L. P.;Zhu, T. J.;Zhao, X. B.
V-VI compounds have been widely investigated as promising thermoelectric materials for room temperature refrigeration. In this paper, we report a systematic study of high performance p-type antimony-telluride-based thermoelectric alloys for mid-temperature power generation. Indium alloying is adopted as an effective approach to widen the band gap and suppress the detrimental bipolar conduction at elevated temperatures. The low Seebeck coefficient of binary antimony telluride, arising from high hole concentration generated by antisite defects, was enhanced by raising the antisite defect energy formation. Meanwhile, the induced alloying scattering significantly reduced the lattice thermal conductivity. Ag acceptor doping was used to further suppress the detrimental bipolar conduction and improve the figure of merit, zT. These combined effects resulted in a peak zT of similar to 0.92 at 710 K for the hot-pressed Ag0.01Sb1.85In0.15Te3 alloy, whereas the average zT(av) of 0.8 was obtained in the temperature range of 500-710 K, indicating a great potential of the alloy for application in mid-temperature thermoelectric power generation. (C) 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.