Effect of solidification rate on microstructure evolution in dual phase microalloyed steel.
Effect of solidification rate on microstructure evolution in dual phase microalloyed steel.
复制标题
DOI：
10.1038/srep35715
复制
发表时间：
2016-10-19
影响因子：
4.6
通讯作者：
Davis CL
中科院分区：
文献类型：
--
作者：
Kostryzhev AG;Slater CD;Marenych OO;Davis CL
In steels the dependence of ambient temperature microstructure and mechanical properties on solidification rate is not well reported. In this work we investigate the microstructure and hardness evolution for a low C low Mn NbTi-microalloyed steel solidified in the cooling rate range of 1–50 Cs−1. The maximum strength was obtained at the intermediate solidification rate of 30 Cs−1. This result has been correlated to the microstructure variation with solidification rate.
登录
查看更多内容
影响因子：
1.8
作者：
Matsuzaki, A;Bhadeshia, HKDH
通讯作者：
Bhadeshia, HKDH
影响因子：
1.8
作者：
Oikawa, Katsunari;Sasaki, Tomoyuki;Ishida, Kiyohito
通讯作者：
Ishida, Kiyohito
影响因子：
1.8
作者：
Wang, Ruizhen;Garcia, C. I.;Deardo, A. J.
通讯作者：
Deardo, A. J.
影响因子：
1.8
作者：
Reid, M;Phelan, D;Dippenaar, R
通讯作者：
Dippenaar, R
DOI：
10.1016/j.msea.2014.12.069
发表时间：
2015-03-11
影响因子：
6.4
作者：
Daamen, Markus;Haase, Christian;Hirt, Gerhard
通讯作者：
Hirt, Gerhard