Metal oxide heteroepitaxy: Stranski-Krastanov growth for iron oxides on Pt(111)
Metal oxide heteroepitaxy: Stranski-Krastanov growth for iron oxides on Pt(111)
复制标题
DOI：
10.1103/physrevb.59.5201
复制
发表时间：
1999-02
影响因子：
3.7
通讯作者：
W. Weiss;M. Ritter
中科院分区：
文献类型：
--
作者：
W. Weiss;M. Ritter
The epitaxial growth of iron oxide films on Pt (111) substrates was investigated by scanning tunneling microscopy and low-energy electron diffraction. The film growth was accomplished by repeated cycles of iron deposition and subsequent oxidation at p (O 2)= 10− 6 mbar. For oxidation temperatures of 870 K second and third FeO (111) layers grow layer by layer, whereas for oxidation temperatures of 1000 K only one FeO (111) monolayer is formed. On top of the FeO (111) films a homogeneous nucleation of Fe 3 O 4 (111) islands takes place, resulting in a Stranski-Krastanov growth for iron oxides on Pt (111). The islands grow in the Fe 3 O 4 bulk structure laterally much faster than vertically, forming flat platelets with heights up to 100 Å and hexagonal and triangular basal planes 1000–5000 Å in diameter. The islands only expose low index {1 11} and {21 1} facet planes, and their growth can be described by an Ostwald ripening mechanism that takes place during each oxidation cycle. Eventually the islands coalesce and form smooth Fe 3 O 4 (111) films at least 150 Å thick. The atomic and mesoscopic surface roughness of these films depends on the growth temperature, where the latter ranges between 40 and 100 Å on a length scale of 1 μm. By a high-pressure oxidation at p (O 2)= 10− 1 mbar the Fe 3 O 4 (111) films were transformed into well-ordered α− Fe 2 O 3 (0001) films with similar surface morphologies. In all oxide phases formed the hexagonal oxygen (111) planes are aligned to the Pt (111) substrate surface lattice. The film growth is discussed in terms of surface and interfacial energies, oxidation and growth kinetics, as well as thermodynamic stability ranges of the different oxide phases.