Excellent strength-ductility synergy in as-cast Al0.6CoCrFeNi2Mo0.08V0.04 high-entropy alloy at room and cryogenic temperatures
Excellent strength-ductility synergy in as-cast Al0.6CoCrFeNi2Mo0.08V0.04 high-entropy alloy at room and cryogenic temperatures
复制标题
铸态 Al0.6CoCrFeNi2Mo0.08V0.04 高熵合金在室温和低温下具有出色的强度-延展性协同作用
DOI：
10.1016/j.matlet.2021.129778
复制
发表时间：
2021-03
影响因子：
3
通讯作者：
Zhang Zhengrong
中科院分区：
文献类型：
--
作者：
Dong Yong;Duan Shougang;Huang Xuan;Li Chuanqiang;Zhang Zhengrong
采用真空感应熔炼法制备了Al 0. 6CoCrFeNi 2 Mo 0. 08 V0. 04高熵合金。该合金具有枝晶和枝晶间组织，在室温和低温下表现出优异的强度-塑性协同效应。室温屈服强度达400 MPa，延伸率超过39%.随着温度的降低，屈服强度、断裂强度和延伸率都有所提高。最大屈服强度在-196 °C时达到560 MPa，延伸率超过42%。断裂机制主要为韧窝型韧性断裂。
The Al0.6CoCrFeNi2Mo0.08V0.04high-entropy alloy was prepared by vacuum induction melting. The alloy presented dendrite and inter-dendrite microstructure and showed excellent strength-ductility synergy at room and cryogenic temperatures. At room temperature, the yield strength reached 400 MPa while the elongation exceeded to 39%. With the decrease of temperatures, the yield strength, fracture strength, and the elongation were all improved. The maximum yield strength reached 560 MPa at −196 °C and the elongation exceeded 42%. The fracture mechanism was mainly a dimple-type ductile fracture.
登录
查看更多内容
影响因子：
6.2
作者：
Salishchev, G. A.;Tikhonovsky, M. A.;Senkov, O. N.
通讯作者：
Senkov, O. N.
影响因子：
9.4
作者：
Varvenne, Celine;Luque, Aitor;Curtin, William A.
通讯作者：
Curtin, William A.
影响因子：
3
作者：
I. Mazilkin;K. Tsoy;A. Straumal;A. Rodin;B. Baretzky
通讯作者：
I. Mazilkin;K. Tsoy;A. Straumal;A. Rodin;B. Baretzky
直接铸造块体共晶和近共晶高熵合金，在宽温度范围内具有均衡的强度和延展性
影响因子：
9.4
作者：
Lu, Yiping;Gao, Xuzhou;Li, Tingju
通讯作者：
Li, Tingju
通过有序氧配合物增强高熵合金的强度和延展性
影响因子：
64.8
作者：
Lei, Zhifeng;Liu, Xiongjun;Lu, Zhaoping
通讯作者：
Lu, Zhaoping