Annealing of Amorphous Sm5Fe17 Melt-Spun Ribbon
Annealing of Amorphous Sm5Fe17 Melt-Spun Ribbon
复制标题
非晶Sm5Fe17熔纺带材的退火
DOI：
10.2320/matertrans.mbw200781
复制
发表时间：
2008
影响因子：
1.2
通讯作者：
T. Saito
中科院分区：
文献类型：
--
作者：
T. Saito
对Sm 5 Fe 17非晶快淬薄带进行了不同条件的退火处理，得到了亚稳Sm 5 Fe 17相。在873 K ~ 973 K温度下退火0.1 ~ 1h，可获得Sm 5 Fe 17相。然而，退火后的样品包含其他相，如SmFe 2和SmFe 3相，这取决于退火条件。结果表明，在873 K退火1h后，样品主要由Sm 5 Fe 17相组成。在1073 K下退火0.1h或0.3h也可得到Sm 5 Fe 17相，但在1073 K下退火1h会导致亚稳Sm 5 Fe 17相分解，形成Sm 2Fe 17和SmFe 3平衡相。
An amorphous Sm 5 Fe 17 melt-spun ribbon was annealed under various conditions to obtain the metastable Sm 5 Fe 17 phase. The Sm 5 Fe 17 phase could be obtained by annealing at temperatures between 873 K and 973 K for 0.1-1 h. However, the annealed specimens contained other phases such as the SmFe 2 and SmFe 3 phases depending on the annealing conditions. It was found that the specimen annealed at 873 K for 1 h consisted mostly of the Sm 5 Fe 17 phase. The Sm 5 Fe 17 phase could also be obtained by annealing the amorphous Sm 5 Fe 17 melt-spun ribbon at 1073 K for 0.1 h or 0.3 h, but annealing at that temperature for 1 h resulted in decomposition of the metastable Sm 5 Fe 17 phase and formed the equilibrium Sm 2 Fe 17 and SmFe 3 phases.
影响因子：
3.2
作者：
SAGAWA, M;FUJIMURA, S;MATSUURA, Y
通讯作者：
MATSUURA, Y