Change of Nitrogen Content in the Molten Steel during CaO Powder Blowing
Change of Nitrogen Content in the Molten Steel during CaO Powder Blowing
复制标题
DOI：
10.1002/srin.200300157
复制
发表时间：
2003-01
影响因子：
2.2
通讯作者：
M. Numata;Yoshihiko Higuchi;S. Fukagawa
中科院分区：
文献类型：
--
作者：
M. Numata;Yoshihiko Higuchi;S. Fukagawa
在减压条件下，分别向钢液中吹入CaO粉和氩气，测定了钢液中氮的脱附速率。在MgO坩埚中用高频感应炉熔炼15kg电解铁，熔体温度保持在1873K。
The rates of nitrogen desorption from molten steel were measured with the blow of CaO powder or argon gas onto the melts under reduced pressure. 15kg of electrolytic iron was melted in a MgO crucible by a high frequency induction furnace and the temperature of the melt was held at 1873 K.