Pb electrodeposition from PbO in the urea/1-ethyl-3-methylimidazolium chloride at room temperature
Pb electrodeposition from PbO in the urea/1-ethyl-3-methylimidazolium chloride at room temperature
复制标题
室温下尿素/1-乙基-3-甲基氯化咪唑鎓中 PbO 电沉积 Pb
DOI：
10.1039/c6ra27383a
复制
发表时间：
2017-01
期刊：
影响因子：
3.9
通讯作者：
Zhaowen Wang
中科院分区：
文献类型：
--
作者：
Wencai He;Aimin Liu;Jinzhao Guan;Zhongning Shi;Bingliang Gao;Xianwei Hu;Zhaowen Wang
In this study, we dissolved PbO in a new electrolyte urea/1-ethyl-3-methylimidazolium chloride (EMIC) and electrochemically extracted Pb. The electrochemical behavior of lead was investigated using chronoamperometric and cyclic voltammetric techniques. The cyclic voltammograms illustrated that lead reduction is quasi-reversible and follows a single-step, two-electron transfer process. The chronoamperometric experiments showed that lead reduction in the PbO–urea/EMIC system follows a 3D instantaneous nucleation and a diffusion-controlled growth at 353 K. The diffusion coefficient was 1.67 × 10−8 cm2 s−1. The effect of temperature on the electrochemical behavior of lead was investigated. Results showed that electrode reaction becomes more reversible as temperature increases from 343 to 373 K. The diffusion coefficients increase with increasing temperature and obey the Arrhenius' law. The activation energy is estimated to be 38 kJ mol−1. Electrodeposition experiments were conducted on tungsten substrates at different negative potentials and various temperatures. Scanning electron microscopy (SEM) images of electrodeposits showed that the Pb particles became smaller and are more densely distributed at more negative potentials and higher temperatures. The obtained electrodeposits were metallic lead, as verified by X-ray diffraction (XRD) and energy dispersive spectroscopy (EDS).
登录
查看更多内容
不同含PbO氯化胆碱-尿素低共熔溶剂电沉积形貌控制制备铅粉
影响因子：
6.7
作者：
Yan Li;Ding Wang;Cancan Qi;Yafei Jie
通讯作者：
Yafei Jie
DOI：
10.1016/s1003-6326(11)60874-1
发表时间：
2011-06
影响因子：
4.5
作者：
Yingying Gu;Qiong-hua Zhou;Tian-zu Yang;W. Liu;Duchao Zhang
通讯作者：
Yingying Gu;Qiong-hua Zhou;Tian-zu Yang;W. Liu;Duchao Zhang
影响因子：
3.7
作者：
T. Ohba;K. Hata;V. Chaban
通讯作者：
T. Ohba;K. Hata;V. Chaban
影响因子：
2.9
作者：
J. Mostany;J. Parra;B. Scharifker
通讯作者：
J. Mostany;J. Parra;B. Scharifker
影响因子：
6.6
作者：
C. Ehlers;U. König;G. Staikov;J. Schultze
通讯作者：
C. Ehlers;U. König;G. Staikov;J. Schultze