High temperature fretting wear of a Ti alloy/CuNiIn contact
High temperature fretting wear of a Ti alloy/CuNiIn contact
复制标题
DOI：
10.1016/j.surfcoat.2008.08.043
复制
发表时间：
2008-12
影响因子：
5.4
通讯作者：
C. Mary;S. Fouvry;J. M. Martín;B. Bonnet
中科院分区：
文献类型：
--
作者：
C. Mary;S. Fouvry;J. M. Martín;B. Bonnet
Fretting wear is a surface degradation process invariably observed when two contacting bodies are subjected to small amplitude oscillatory movements. In the blade/disk contact of aero-engines especially, movements induced by the engine regime changes may lead to critical wear. In order to limit friction and protect components, motorists usually use a thick and soft CuNiIn layer (150 µm). This system is subjected to high contact pressure (up to 600 MPa) and high temperatures (up to 500 °C). This paper focuses on the identification of the degradation mechanisms of such a system. An experimental layout was designed to perform fretting wear tests up to 500 °C. A punch (commercial Ti17) on plane (Ti6242 coated with CuNiIn) geometry was chosen and fretting tests were performed at several temperatures (20 °C, 250 °C, 350 °C and 450 °C). Surface damage evolution was followed by 3D profilometry and several analyses (SEM, EDS, µ-hardness) were conducted on the surface and on cross-sections. Based on the results, specific degradation mechanisms were identified for this Ti17/CuNiIn contact at high temperatures, suggesting that the tribochemical effects should be considered in the fretting wear models.