Photocatalytical removal of inorganic and organic arsenic species from aqueous solution using zinc oxide semiconductor.
Photocatalytical removal of inorganic and organic arsenic species from aqueous solution using zinc oxide semiconductor.
复制标题
DOI：
10.1039/c2pp25231g
复制
发表时间：
2013-04
期刊：
影响因子：
--
通讯作者：
Hernández-Ramírez A
中科院分区：
文献类型：
--
作者：
Rivera-Reyna N;Hinojosa-Reyes L;Guzmán-Mar JL;Cai Y;O'Shea K;Hernández-Ramírez A
在紫外光（350 nm）和溶胶-凝胶技术合成的 ZnO 水悬浮液存在下，研究了光催化去除亚砷酸盐 [As(III)] 和一甲基胂酸 [MMA(V)]。光催化去除这些强效砷化合物可以有效、快速地矿化为毒性较小的无机砷酸盐 [As(V)]。评估了 ZnO 负载量和溶液 pH 值对 UV/ZnO 光催化过程处理效率的影响。在催化剂负载量分别为 0.25 和 0.50 g L−1、溶液 pH 值分别为 7 和 8 时，观察到去除 5 mg L−1 [As(III)] 和 [MMA(V)] 水溶液的最佳条件。在这些条件下，将光催化剂溶胶-凝胶 ZnO 的活性与 TiO2 Degussa P25 和商用 ZnO 催化剂进行了比较。结果表明，溶胶-凝胶合成的 ZnO 具有高吸附能力，可增强水样中砷的去除能力，表明该催化剂是处理砷污染地下水的有前景的材料。
The photocatalytic removal of arsenite [As(III)] and monomethylarsonic acid [MMA(V)] was investigated in the presence of UV light (350 nm) and aqueous suspensions of ZnO synthesized by the sol–gel technique. Photocatalytic removal of these potent arsenic compounds results in the effective and rapid mineralization to less toxic inorganic arsenate [As(V)]. The effect of ZnO loading and solution pH on the treatment efficiency of the UV/ZnO photocatalytic process was evaluated. The optimal conditions for the removal of 5 mg L−1 [As(III)] and [MMA(V)] aqueous solutions were observed at catalyst loadings of 0.25 and 0.50 g L−1 with solution pH values of 7 and 8, respectively. Under these conditions, the activity of photocatalyst sol–gel ZnO was compared with TiO2 Degussa P25 and commercial ZnO catalyst. The results demonstrate that the high adsorption capacity of ZnO synthesized by sol–gel gives enhanced removal of arsenic species from water samples, indicating that this catalyst is a promising material for treatment of arsenic contaminated groundwater.
登录
查看更多内容
影响因子：
11.4
作者：
Jing, CY;Liu, SQ;Meng, XG
通讯作者：
Meng, XG
影响因子：
5.3
作者：
Lizama, C;Freer, J;Mansilla, HD
通讯作者：
Mansilla, HD
影响因子：
6.9
作者：
Sakthivel, S;Neppolian, B;Murugesan, V
通讯作者：
Murugesan, V
影响因子：
2.5
作者：
Salinas-Guzman, R. R.;Guzman-Mar, J. L.;Hernandez-Ramirez, A.
通讯作者：
Hernandez-Ramirez, A.
影响因子：
11.4
作者：
Ferguson, MA;Hoffmann, MR;Hering, JG
通讯作者：
Hering, JG