Well-defined SiO2-coated Fe2Co nanoparticles prepared by reduction with CaH2
Well-defined SiO2-coated Fe2Co nanoparticles prepared by reduction with CaH2
复制标题
CaH2 还原制备明确的 SiO2 包覆 Fe2Co 纳米颗粒
DOI：
10.1039/c5ra20306f
复制
发表时间：
2015
期刊：
影响因子：
3.9
通讯作者：
S. Yamamoto and M. Tsujimoto
中科院分区：
文献类型：
--
作者：
S.Yamamoto;Y.Kusano;S. Yamamoto and M. Tsujimoto
通过将CoFe2O4纳米粒子与CaH2还原，成功制备了性能良好的CoFe2O4纳米粒子。使用CaH2降低还原温度是保持初始纳米颗粒完整的良好形态的必要条件。使用具有COOH基团的硅烷偶联剂进行表面改性，可以获得优异的水分散性，从而通过EDC/NHS化学等成熟的过程促进随后与各种分子的功能化。所获得的二氧化硅包覆的Fe2Co纳米颗粒具有可控的形态、耐蚀性、软磁性能和易于后功能化的特点，有望成为电磁、生物和医学应用的基石。
Well-defined SiO2-coated Fe2Co nanoparticles have been successfully prepared by the reduction of SiO2-coated CoFe2O4 nanoparticles with CaH2. Lowering the reducing temperature by using CaH2 is essential to keep the well-defined morphology of the starting nanoparticles intact. Surface modification with a silane coupling agent which has COOH groups has led to excellent aqueous dispersibility that facilitates subsequent functionalization with a variety of molecules via well-established processes such as EDC/NHS chemistry. The obtained SiO2-coated Fe2Co nanoparticles equipped with controlled morphology, corrosion resistivity, soft magnetic properties, and easy post-functionalization are expected to serve as a building block for electromagnetic, biological, and medical applications.
登录
查看更多内容
影响因子：
15
作者：
C. Tassel;Takashi Watanabe;Y. Tsujimoto;N. Hayashi;A. Kitada;Yuji Sumida;Takafumi D. Yamamoto;H. Kageyama;M. Takano;K. Yoshimura
通讯作者：
C. Tassel;Takashi Watanabe;Y. Tsujimoto;N. Hayashi;A. Kitada;Yuji Sumida;Takafumi D. Yamamoto;H. Kageyama;M. Takano;K. Yoshimura
CaH2辅助低温合成负载金属磁性纳米颗粒的多壁碳纳米管。
影响因子：
4.9
作者：
Liis Seinberg;S. Yamamoto;M. Tsujimoto;Y. Kobayashi;M. Takano;H. Kageyama
通讯作者：
H. Kageyama
影响因子：
15
作者：
Sun, SH;Zeng, H;Li, GX
通讯作者：
Li, GX
溶胶凝胶法制备二氧化硅基纳米晶铁钴合金
DOI：
10.1016/s0022-3093(01)00639-1
发表时间：
2001
期刊：
影响因子：
--
作者：
G. Ennas;M. Casula;A. Falqui;D. Gatteschi;G. Marongiu;G. Piccaluga;C. Sangregorio;G. Pinna
通讯作者：
G. Pinna
影响因子：
16.6
作者：
Kageyama, Hiroshi;Watanabe, Takashi;Andre, Gilles
通讯作者：
Andre, Gilles